1) H pull-out
H抽出力
1.
The results showed that the t_(10)and t_(90)of rubber compound extended a little by using superfine active kaolin partly instead of carbon black in inner ply and outer ply compounds,and the physical properties of vulcanizate and H pull-out after aging changed little;the endu-rance of finished tire improved and the cost of rubber compound reduced.
结果表明,在内层和外层帘布胶中以超细活性高岭土部分替代炭黑后,胶料的t10和t90稍有延长,硫化胶的物理性能及老化后H抽出力基本相当;成品轮胎耐久性能提高,胶料成本降低。
2.
The results showed that the scorch time extended,the curing speed reduced,the anti-reversion improved,and the better tensile,elongation and tear properties were obtained using TBSI instead of TBBS by equal weight in the upper bead filler compound;and the scorch time extended,t_(90) reduced,the permanent tensile set decreased and the H pull-out changed little using 1 phr of TBSI instead of 1.
在胎体胶配方中以 1份促进剂TBSI替代 1 2 5份促进剂DZ ,胶料的焦烧时间延长 ,t90 缩短 ,硫化胶的拉断永久变形减小 ,H抽出力相当。
2) H pull-out force
H抽出力
1.
The results showed that when compared to the dry cobalt decanoate,the wet cobalt decanoate gave NR vulcanizate higher H pull-out force,lower H pull-out force loss after hot air aging and brine aging and similar physical properties.
结果表明,与干法工艺生产的癸酸钴相比,采用湿法工艺生产的癸酸钴可提高NR硫化胶的H抽出力,经热空气老化和盐水老化后硫化胶的H抽出力下降率较小,其它物理性能基本相当。
3) adhesion by H test
H抽出值
1.
Experiments on changing fomula of nylon6 dip solution find that there has a constant ratio betwen RFL viscosity and adhesion by H test of nylon6 dipped cord fabric.
通过对浸胶液处方的调整试验 ,发现RFL液粘度与帘子布H抽出值之间存在比例关系 ,从而可以用RFL液粘度推算帘子布的H抽出值大
4) H-test
"H"抽出
6) drawing force
抽出力
补充资料：氯仿抽出物
分子式：
CAS号：
性质：抽取丙酮抽出物后的硫化橡胶，再用氯仿在一定条件下所抽出的物质。其中主要包括不被丙酮抽出的沥青、焦油、矿物油以及少量的橡胶烃。硫化橡胶中的氯仿抽出物可以采用快速抽提器或索氏抽提器进行测定。
CAS号：
性质：抽取丙酮抽出物后的硫化橡胶，再用氯仿在一定条件下所抽出的物质。其中主要包括不被丙酮抽出的沥青、焦油、矿物油以及少量的橡胶烃。硫化橡胶中的氯仿抽出物可以采用快速抽提器或索氏抽提器进行测定。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条