1)  Cr/C
Cr/C
1.
Effects of Cr/C on Property of High Chromium Wear Resistance and Corrosion Resistance Cast Iron with 4%Ni;
Cr/C对含4%Ni高铬耐磨耐蚀铸铁性能的影响
2.
Effects of Cr/C on the Microstructure of High Chromium Wear Resistant and Corrosion Resistant Cast Iron with 4 Percent of Nickel;
Cr/C对含4%Ni高铬耐磨耐蚀铸铁组织的影响
3.
In this paper, the effect of Ni, Cu and Cr/C on microstructure and properties of high chromium ferroalloy is explored by the method of contrast experiment, and the development of a new high chromium ferroalloy with wear and corrosion resistance is finished.
本文利用对比实验的方法探讨了不同质量分数的Ni、Cu以及Cr/C对高铬铁合金显微组织和性能的影响规律,完成了新型耐磨耐蚀高铬铁合金的研发。
2)  Cr-C
Cr-C
1.
Dependence of Structure Stability of Electrodepositing Amorphous Cr-C and Ni-P onC,P Contents;
电沉积Cr－C，Ni－P非晶结构稳定性对C，P含量的依赖性
3)  Ni-Cr-C
Ni-Cr-C
1.
Wear resistant Cr_7C_3/ -Cr_7C_3 composite coating was fabricated on commercial Q235 plain carbon steel substrate from Ni-Cr-C elemental powder blends using plasma jet cladding.
以Ni-Cr-C混合合金粉末为添加原料,采用等离子熔覆技术,在普通机械制造用钢Q235表面形成了以初生块状金属陶瓷Cr7C3为硬质耐磨增强相,以强韧性良好的γ/Cr7C3共晶为基体的复合材料冶金涂层,分析了涂层的显微组织和硬度,在室温干滑动磨损条件下测试了其耐磨性。
4)  Cr/C ratio
Cr/C比
1.
Under laboratory conditions,the influence of Cr/C ratio and heat treatment process on the abrasive wear resistance of high chromium cast iron was studied.
在实验室条件下,研究了Cr/C比及热处理工艺对高铬铸铁抗冲击磨粒磨损性能的影响。
5)  Cr-C alloy
CrC合金
6)  Fe Cr C system
Fe-Cr-C系
参考词条
补充资料：(oc-6-11)-chromium carbonyl (cr(co)6
CAS：13007-92-6
分子式：C6CrO6
分子质量：220.06
沸点：220℃
熔点：150-155℃
中文名称：六羰基铬
英文名称：(OC-6-11)-Chromium carbonyl；chromium carbonyl；(oc-6-11)-chromium carbonyl (cr(co)6；chromium carbonyl (oc-6-11)；chromium hexacarbonyl；hexacarbonyl chromium；chromiumcarbonyl；Chromium carbonyl,(OC-6-11)-；Chromium carbonyl；Hexacarbonylchromium
说明：补充资料仅用于学习参考，请勿用于其它任何用途。