1) draw ratio
拉伸比
1.
The stability of Nylon 66 technical yarn properties was obtained by adjusting of spinning viscosity, draw ratio, take-up tension and godet temperature.
通过调整纺丝黏度、纺丝拉伸比、卷绕张力、拉伸辊温度等可以对尼龙66工业丝物理性能的稳定起到很重要的作用,尤其是可以使其均匀性提高,三项主要物性指标工序能力控制指数(CPK)达到1级以上。
2.
The results showed that the relative molecular weight and its distribution of polypropylene, isotacticity, spinning temperature, quenching speed, draw ratio, drawing godet temperature and oiling amount had evident effect on yarn irregularity.
结果表明,聚丙烯的相对分子质量及其分布、等规度和纺丝温度、冷却吹风速度、拉伸比率、上热盘温度以及上油量等对纤维不匀率产生明显的影响。
3.
The influences of draw ratio(λ)and compatibilizer contents(C g)on PA66 fiberization and mechanical properties of the composites were investigated.
用挤出 -拉伸 -注塑法制备了PP/PA66原位复合材料 ,研究了拉伸比 (λ)和增容剂用量 (Cg)对PA66成纤性和材料力学性能的影响。
3) hot stretching ratio
热拉伸比
4) principal extension ratio
主拉伸比
5) draft ratio
牵伸比;拉伸比
6) mean specific stress
拉伸比应力
1.
The effect of the pretreatment process on slenderizing wool fibres was analyzed and the criterions for evaluating the pretreatment technology were established,including mean specific stress,the breakage elongation and the surface damage.
分析了羊毛拉伸细化预处理工艺的作用 ,建立了预处理工艺条件的选择依据 ,包括平均拉伸比应力、断裂伸长率和纤维的表面损伤。
补充资料：拉伸比
分子式：
CAS号：
性质：又称拉伸比，拉伸倍数。高聚物经纺丝成形后的初生纤维经过拉伸工序后其长度与原长度的比值。通常以拉伸过程中纤维的输出速度与喂入速度之比表示。完整的概念是拉伸行为发生在两部分：一是喷丝头拉伸，即纺丝熔体或液体流出喷丝孔的线速度，与卷绕速度之比，二是上述的初生纤维拉伸。在工艺中此两种拉伸需恰当控制。
CAS号：
性质：又称拉伸比，拉伸倍数。高聚物经纺丝成形后的初生纤维经过拉伸工序后其长度与原长度的比值。通常以拉伸过程中纤维的输出速度与喂入速度之比表示。完整的概念是拉伸行为发生在两部分：一是喷丝头拉伸，即纺丝熔体或液体流出喷丝孔的线速度，与卷绕速度之比，二是上述的初生纤维拉伸。在工艺中此两种拉伸需恰当控制。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。