1) core/shell ratios
核壳比
1.
In this paper,cationic silicon dioxide/polyurethane (SiO2/PU) nanocomposites dispersions with different core/shell ratios were prepared in-situ by sol-gel,and the phase behavior of them were studied by thermal analysis.
本文采用溶胶-凝胶法在位制备了不同核壳比(正硅酸乙酯与聚氨酯的质量比)的阳离子型二氧化硅/聚氨酯(S iO2/PU)纳米复合物水分散液;并利用热分析法对不同核壳比的S iO2/PU纳米复合物的相行为进行了研究。
2) core-shell
核壳
1.
Preparation of reduced symmetrical SiO_2/Au core-shell nanoparticles and their plasmonic properties;
对称性降低的SiO_2/Au核壳结构纳米粒子的制备及其表面等离子共振特性
2.
The preperation of core-shell nanopowder material by one-step hydrothermal method;
一步水热法制备核壳型纳米粉体研究
3.
Development of Core-shell Emulsion Polymerization;
核壳型乳液聚合研究进展
3) core-shell
核-壳
1.
High concentration(as high as 40 mg/mL) of core-shell PMAA/HEC polymeric nanoparticles are prepared via one-step template polymerization by using hydroxyethyl cellulose(HEC) as the template,and methacrylic acid(MAA) as the monomer.
以羟乙基纤维素(HEC)为大分子模板,选用甲基丙烯酸(MAA)单体,通过模板聚合一步反应,制备了较高浓度(40 mg/mL)的核-壳结构聚合物纳米微球溶液。
2.
The mechanism of core-shell emulsion polymerization was brifly introduced,which included grafting,interpenetrating network formation and ionic bonding.
简要介绍了核-壳型乳液聚合机理,包括接枝机理,互穿网络聚合机理及离子键合机理。
3.
The mechanical property of epoxy resin modified with silicone particles and core-shell parti.
以此为种子乳液进一步反应,使甲基三甲氧基硅烷(MTMS)在种子乳胶粒表面反应形成硅树脂壳层,得到硅树脂包覆硅橡胶的核-壳乳胶粒子。
4) core/shell
核/壳
1.
The toughening of HIPS is studied by blending it with a polybutylacrylate/polyethylmethacrylate core/shell structure elastomer particles, an a new mechanism of toughening isproposed.
本文研究了聚丙烯酸丁酯／聚甲基丙烯酸乙酯核／壳结构弹性体粒子对ＨＩＰＳ的增韧作用，提出了一个新的增韧机理。
5) Core/shell
核壳
1.
PSA@Fe3O4 doped CdS core/shell nanocomposite was prepared for the first time by a simple wet-chemistry route.
用简单的湿化学方法首次制备了PSA@Fe3O4doped CdS核壳结构复合微球。
2.
The core/shell polyurethane-polyacrylate emulsion(PUA) was synthesized by seed emulsion polymerization with using waterborne PU as the seed emulsion and PA as the monomer.
以水性聚氨酯(PU)为种子乳液,以丙烯酸酯(PA)为聚合性单体,采用种子乳液聚合法合成核壳结构聚氨酯-聚丙烯酸酯乳液(PUA)。
6) core-shell particles
核壳粒子
1.
Preparation and characterization of nano-Ag /PS core-shell particles;
纳米银/聚苯乙烯核壳粒子的制备与表征
2.
P(APU-BA)/PMMA core-shell particles were prepared by polymerization of self-made acrylate polyurethane(APU) and seed emulsion.
采用自制的丙烯酸酯化聚氨酯(APU)和种子乳液聚合的方法,制备了一种P(APU-BA)/PMMA型的核壳粒子。
3.
Layer-by-layer (LbL) assembled core-shell particles are currently studied immensely due to their advantages of tailored dimensions and compositions.
本文综述了基于层层自组装和胶体模板以及采用各种化学和物理方法直接除去核制备磁性复合核壳粒子和空腔球体。
参考词条
补充资料：不锈钢包壳核燃料
分子式：
CAS号：
性质：奥氏体不锈钢在高温水、氦气和液态金属钠等介质中具有良好的耐腐蚀性能和适当的高温强度，加工工艺成熟，但因其热中子吸收截面较大，在热中子堆中只能作为浓缩铀燃料的包壳。在快中子增殖堆中，大多数采用不锈钢包壳的氧化物燃料。在所选定的工作温度范围内，不锈钢包壳材料与冷却剂钠能够相容，而且成本低。
CAS号：
性质：奥氏体不锈钢在高温水、氦气和液态金属钠等介质中具有良好的耐腐蚀性能和适当的高温强度，加工工艺成熟，但因其热中子吸收截面较大，在热中子堆中只能作为浓缩铀燃料的包壳。在快中子增殖堆中，大多数采用不锈钢包壳的氧化物燃料。在所选定的工作温度范围内，不锈钢包壳材料与冷却剂钠能够相容，而且成本低。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。