1)  oil repellency
拒油
1.
The principles of textile water and oil repellency are discussed in the paper.
文章论述了纺织品的拒水拒油机理以及整理剂的选择,并应用纳米材料和有机氟树脂复配的整理剂对纯毛绒线进行了拒水拒油整理工艺的研究,采用经实验得到的整理优化工艺条件,对纯毛绒线进行整理,可赋予绒线优良的拒水拒油性能且具有耐久性,整理对后绒线的强力没有影响。
2.
The optimum process had been investigated and under the optimum process the water repellency,and oil repellency of the fabric were greatly improved.
文章论述了织物的拒水拒油机理以及拒水拒油整理剂的选择,采用纳米材料和有机氟树脂复配,利用正交试验设计实验方案对毛织物进行了拒水拒油整理,得到了提高毛织物的拒水拒油整理优化工艺条件,整理后的毛织物经AATCC-22和AATCC-11标准检测表明,具有优良的拒水拒油性和耐久性。
2)  Oil-repellent
拒油
1.
Water-and oil-repellent finishing of nylon-cotton union fabrics;
锦/棉交织物的拒水拒油整理
2.
This text analysed the shortcomings of traditional organic water-and-oil-repellent finishing, and researched the sol-gel method which developed the silicon dioxide water-and-oil-repellent finishing agent, and chosen the optimal relationship of all the reactants and activators and reaction conditions.
阐述了传统的有机拒水拒油整理的居多缺点,研究了溶胶凝胶法制备纳米二氧化硅拒水拒油整理剂的方法,得出各反应物和催化剂之间的最佳物质的量的比及反应条件。
3)  oil repellent
拒油
1.
The Ploysulfonamide(PSA)fabric is finished by a water and oil repellent organic fluorine AG7600 and a cross-linking agent melamine formaldehyde resin.
采用含氟拒水拒油整理剂AG-7600,交联剂三聚氰胺甲醛对芳砜纶织物进行拒水拒油整理,经过试验,得到芳砜纶织物拒水拒油整理的最优工艺条件为AG-7600整理剂质量分数为6%、三聚氰胺甲醛交联剂质量分数为2%、焙烘温度为170℃、焙烘时间为1min,整理后织物获得良好的拒水拒油性能及耐久性。
4)  water-and oil-repellency
拒水拒油
1.
The water-and oil-repellent multi-functional finishing agent DM-3640C showed,when used on cotton poplin,good water-and oil-repellent results could be obtained at low dosage(30 g/L DM-3640C and 4 g/L coupling agent DM-3911),water-repellency continuousness was good,the electrolyte influence on water-and oil-repellency was not obvious and wide pH and temperature r.
介绍了有机氟树脂的结构与性能特征,分析了其对织物防水防油的机理,拒水拒油多功能整理剂DM-3640C用于棉府绸整理时,在较低用量下(DM-3640C 30 g/L,架桥剂DM-3911 4 g/L)即可获得优良的拒水拒油效果。
5)  Water and oil repellent
拒水拒油
1.
Preparation of cationic short branched-chain perfluoroalkyl-based water and oil repellent finish agent
阳离子型短支链全氟烷基拒水拒油整理剂的制备
2.
It has been known that fluorocarbons have an extremely low surface free energy and they are widely applied for water and oil repellent finishing.
众所周知,氟碳化合物具有极低的表面张力,因此广泛用于拒水拒油整理。
6)  water and oil repellency
拒水拒油
1.
The results indicated that the perfluorooctanoic acid reacted with amino group successfully and the dual layer film showed some extent of water and oil repellency.
采用自组装方法在羟基化硅基底表面制备全氟辛酸/氨基硅烷(PFOA-APTES)自组装双层膜,根据全氟辛酸与氨基硅烷自组装膜末端氨基反应时间的不同,制备3个PFOA-APTES自组装双层膜样品,运用原子力显微镜(AFM)、X-射线光电子能谱(XPS)和接触角测试仪来评价薄膜结构及其拒水拒油性能。