The results showed that the chlorine-induced degradation on PU soft segment occured and C-Cl compound formed under the attack of activated chloric atom.
结果表明，ＰＵ浸氯水后，因受活性氯原子的攻击，ＰＵ大分子软链段的碳－碳键发生断裂，形成碳－氯化合物，添加剂加入后，因与ＰＵ大分子的软链段形成螯合物，从而避免了活性氯原子的攻击，有效地保护了软链段，使氨纶耐氯性能明显改善。
4) chlorocarbon
[英][,klɔ:rə'kɑ:bən] [美][,klɔro'kɑrbən, ,klor-]
氯碳化合物
5) one carbon atom compound
碳一化合物
1.
With abundance resources of coal and natural gas, the synthesis of ethylene glycol from one carbon atom compounds has wide developmental field and applied foreground in China.
我国具有丰富的煤和天然气资源,以碳一化合物合成乙二醇(EG)具有广阔的发展空间和应用前景。
6) primary carbide
一次碳化物
1.
The results showed that adding Cr powder and graphite to Ni-based alloy powder can yield primary carbide precipitate in the surfacing layer,which obviously increases its hardness.
结果表明,在镍基合金粉中加入铬粉和石墨,堆焊层中析出了一次碳化物,可显著提高堆焊层的宏观硬度;随铬粉和石墨加入量的增加,堆焊层中一次碳化物的析出量随之增加,堆焊层的宏观硬度相应提高,最高可达62HRC,是镍基合金粉光束堆焊层的2。
2.
The results show that adding Cr powder and graphite to Ni-based alloy powder can make primary carbide precipitate in surfacing layer, which observably increase the hardness of surfacing layer.
研究结果表明,在镍基合金粉中加入铬粉和石墨,堆焊层中析出了一次碳化物,可显著提高堆焊层的宏观硬度;随铬粉和石墨加入量的增加,堆焊层中一次碳化物的析出量随之增加,堆焊层的宏观硬度相应提高,最高可达HRC62,是镍基合金粉光束堆焊层的2。
补充资料：吡啶烷基衍生物蒸馏残余物氯化苄季铵化物
CAS：97375-31-0
中文名称：吡啶烷基衍生物蒸馏残余物氯化苄季铵化物
英文名称：Pyridine, alkyl derivs., distn. residues, benzyl chloride-quaternized
中文名称：吡啶烷基衍生物蒸馏残余物氯化苄季铵化物
英文名称：Pyridine, alkyl derivs., distn. residues, benzyl chloride-quaternized
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条