1) spinning solution
纺丝原液
1.
Stability of spinning solution of melamine formaldehyde fiber;
三聚氰胺甲醛纤维纺丝原液的稳定性
2.
Study on the rheological behavior of viscose/Na_2SiO_3·9H_2O spinning solution
纤维素/硅酸钠纺丝原液流变性能的研究
3.
The non-newtonian index of the spinning solutions at different temperatures have been obtained.
利用RS150L型流变仪研究了干纺氨纶纺丝原液的流变性能。
2) spinning dope
纺丝原液
1.
Measurement of solid content and NaSCN content in PAN spinning dope by pressed film method;
压膜法测腈纶纺丝原液的固体含量与NaSCN含量
2.
Preparation and wet spinning process for chitosan spinning dope;
壳聚糖纺丝原液制备及湿法纺丝工艺初探
3.
This paper reviewed methods of reducing apparent viscosity of chitosan spinning dope at home and abroad.
综述了国内外降低甲壳胺纺丝原液表观粘度的方法,通过试验,提出了两种降低甲壳胺纺丝原液表观粘度的方法:加入三聚氰胺法、短时间升温法,并对这两种方法进行了分析探讨。
3) blended solution
共混纺丝原液
1.
The viscosity and rheology of blended solutions were determined.
明胶与聚乙烯醇(PVA)溶液共混得到不同配比的纺丝原液,通过测定其流变性与共混膜的力学性能,得到优化明胶-PVA共混纺丝原液固含量比为1。
4) solution spinning
溶液纺丝
1.
The CC solution with 7% mass fraction was exposed to solution spinning in presence of 7% dilute sulfuric acid as coagulation bath after filtration and deaeration.
探索了尿素对纤维素氨基甲酸酯(CC)/氢氧化钠溶液(CC溶液)的增溶作用,考察了不同浓度CC溶液的流变性能,选择CC质量分数为7%的溶液经过滤、脱泡后,以7%的稀硫酸为凝固浴进行溶液纺丝。
2.
The characteristics of melt-spinning,solution spinning,electrospinning,supercritical fluid technique and gelation freeze-drying are summarized in detail,and the effect of molding process on the morphologic structure and performance of the fibers are discussed.
介绍了高强度、可控降解周期的聚乳酸及其共聚物、共混物纤维的成型方法和纤维的应用情况;阐述了熔融纺丝、溶液纺丝、静电纺丝、超临界流体法、凝胶冻干等纤维成型方法的特点;评价了成型工艺对纤维形态结构和性能的影响、研究聚乳酸纤维的新方法、新成果以及高性能聚乳酸纤维在生物医学领域、日用工业等领域的应用前景。
3.
PLA fibers can spin by two conventional methods: solution spinning and melt spinning.
聚乳酸纤维是可生物降解的新型绿色纤维,它可由常见的纤维成型加工工艺———溶液纺丝和熔融纺丝制得。
5) spinning solution
纺丝溶液
1.
Study on capability of regenerative cellulose from cellulose/phosphoric acid spinning solution;
纤维素/磷酸纺丝溶液再生性能研究
2.
The effect of relative molecular weight of polymer and the concentration, temperature of polyacrylonitrile spinning solution on the flow curves lg η a-lg ,non-Newtonian index, viscous activation energy and structural viscosity index was studied.
研究了聚丙烯腈 (PAN )纺丝溶液的浓度、温度及聚合物相对分子质量对纺丝溶液的 lgηa ～lgγ流动曲线、粘流活化能、非牛顿指数和结构粘度指数的影响。
3.
The researches have been conducted by using capillary rheometer on the rheolo_gical property of PANI spinning solution and its influential factors.
采用毛细管流变仪对还原式聚苯胺 /N_甲基吡咯烷酮纺丝溶液的流变性质及其影响因素进行了研究 。
6) emulsion spinning
乳液纺丝
补充资料：纺丝原液
分子式：
CAS号：
性质：化学纤维的高聚物在纺丝成形前必须配制成熔体或溶液的流体，称为纺丝原液，或纺丝浆液(常指纤维素醋酸酯纺丝原液)。
CAS号：
性质：化学纤维的高聚物在纺丝成形前必须配制成熔体或溶液的流体，称为纺丝原液，或纺丝浆液(常指纤维素醋酸酯纺丝原液)。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。