1) calcium and magnesium silicate
钙镁硅酸盐
1.
The equilibrium concentration of Ca2+ and Mg2+ in a calcium and magnesium silicate(CaO·mSiO2,MgO·mSiO2,m is the modulus) saturated solution was determined with an ICPS-1000IV high frequency plasma emission spectrograph at a certain temperature.
借助高频等离子体发射光谱分别测定了一定温度下钙镁硅酸盐(CaO。
2) silicic acid, calcium magnesium salt
硅酸钙镁盐
3) calcium magnesium silicate
硅酸钙镁
4) magnesium silicate
镁硅酸盐
1.
Composition of nanosized complex antibacterials with magnesium silicate carrier and its applications in household and personal care products;
镁硅酸盐复合纳米抗菌剂及其在日化领域中的应用
6) calcium magnesium acetate salt
醋酸钙镁盐
1.
The production process of calcium magnesium acetate salt(CMA) by means of reaction of glacial acetate acid with dolomite was studied.
研究了冰醋酸与白云石直接反应制醋酸钙镁盐(CMA),当水/冰醋酸摩尔比为6。
2.
The snow-melting agent on road was studied for calcium magnesium acetate salt as mail material.
本文以醋酸钙镁盐为主要原料研制了环保型道路融雪剂 ,讨论了原材料的选择、氧化钙与氧化镁的比例、反应温度、添加剂对产品融雪效果的影响 ,并进行了融雪试验 ,达到了环境保护的基本要求 ,并与氯化钠进行了比较试
补充资料：硅酸三钙
分子式：
CAS号：
性质：3CaO·SiO2 白色固体。纯硅酸三钙只在1250～2065℃温度范围内稳定，在2065℃以上不一致熔融为氧化钙和液相，在1250℃以下分解为硅酸二钙和氧化钙。在急冷条件下，硅酸三钙的分解速度较慢，使其可在常温下以介稳态存在。硅酸三钙可由氧化钙和二氧化硅在高温下通过固相反应生成，也可由硅酸二钙和氧化钙反应生成。硅酸三钙是水泥熟料的主要矿物，含量可达50%或更多。
CAS号：
性质：3CaO·SiO2 白色固体。纯硅酸三钙只在1250～2065℃温度范围内稳定，在2065℃以上不一致熔融为氧化钙和液相，在1250℃以下分解为硅酸二钙和氧化钙。在急冷条件下，硅酸三钙的分解速度较慢，使其可在常温下以介稳态存在。硅酸三钙可由氧化钙和二氧化硅在高温下通过固相反应生成，也可由硅酸二钙和氧化钙反应生成。硅酸三钙是水泥熟料的主要矿物，含量可达50%或更多。