1) In_2O_3
In2O3
1.
In_2O_3 nanocones have been in-situ grown on the surface of indium substrates by heating indium grains coated with an Au film at 900～1000 ℃ in air.
以Au作催化剂,将金属铟在空气中加热到900~1 000℃,在单质铟表面制备出In2O3纳米锥。
2.
The In_2O_3 coating by precipitation method to the phosphor was applied to promote the conductivity of particles.
采用高温固相法合成了FED用Y2O3∶Eu红色荧光粉,为提高其导电性,采用表面成膜包覆法对其进行了In2O3包膜研究。
3.
The precursors of In_2O_3 nanorods were prepared by sol-gel technology with the non-ionic surface active agent controlling their morphology.
以非离子表面活性剂作为形貌控制剂,采用溶胶-凝胶法制备In2O3纳米棒前驱物,经500℃煅烧1h,成功制备了长约120nm,直径20nm的In2O3纳米棒。
2) CaO-In_2O_3
CaO-In2O3
1.
Preparation,Structure Attribute And Gas Sensitivity Of CaO-In_2O_3;
采用共沉淀方法,以一定摩尔比的可溶性钙盐和铟盐为源物质,以氢氧化物作为沉淀剂,制备出了CaO-In2O3复合氧化物粉末。
3) In_2O_3/Al_2O_3
In2O3/Al2O3
1.
The Selective Catalytic Reduction of NO by Propene on In_2O_3/Al_2O_3 Catalysts in the Presence of Oxygen;
采用溶胶-凝胶法制备了In2O3/Al2O3氧化物催化剂,对其进行了BET、XRD、XPS及TPD表征。
4) indium oxide leyers
In2O3膜
5) nanosized Sn-In2O3
纳米Sn-In2O3
1.
Nanosized Sn-In2O3 was surface treated to get aqueous nanosized Sn-In2O3 suspension dispersed stably.
纳米Sn-In2O3颗粒经表面处理制得稳定分散的水基Sn-In2O3浆体。
6) doped In_2O_3
掺杂In2O3
补充资料：boron calcium oxide (b4cao7)
CAS：12007-56-6
分子式：B4CaO7
中文名称：四硼酸钙；硼酸钙；硼钙石,水化硼酸钙,硬硼钙石
英文名称：Boron calcium oxide；Calcium borate；boric acid (h2-b4-o7), calcium salt ；boron calcium oxide (b4cao7)；calcium tetraborate；colemanite
分子式：B4CaO7
中文名称：四硼酸钙；硼酸钙；硼钙石,水化硼酸钙,硬硼钙石
英文名称：Boron calcium oxide；Calcium borate；boric acid (h2-b4-o7), calcium salt ；boron calcium oxide (b4cao7)；calcium tetraborate；colemanite
说明：补充资料仅用于学习参考，请勿用于其它任何用途。