1) alinite cement
阿利尼特水泥
1.
The hydraulic properties,mechanical properties and energy-saving characteristic of alinite cement are sum- rnarized.
阿利尼特水泥是一种节能水泥。
2.
The influence of gypsum on the forming of early hydrated product of new white alinite cement added gypsum was studied by means of DTA, XRD and SEM .
利用DTA,XRD,SEM等方法,研究了石膏对新型白色阿利尼特水泥的早期水化产物形成的影响。
3.
Municipal solid waste incinerator (MSWI) fly ash was successfully used as raw material in sintering alinite cement clinker in the laboratory.
以城市垃圾焚烧飞灰(以下简称焚烧飞灰)为主要原料,在实验室电炉里成功烧成了阿利尼特水泥熟料,分析了熟料烧成所需适宜的生料组成和最佳煅烧温度,并研究了石膏掺量对阿利尼特水泥强度影响,以及阿利尼特水泥的标准稠度用水量和凝结时间。
2) alite-rich Portland cement
高阿利特水泥
1.
The effect of slag,fly ash,and calcined shale on setting time,compressive strength,resistivity,composition and microstructure of hydrated product of alite-rich Portland cement were studied.
研究了矿渣、粉煤灰和烧页岩单掺及复掺对高阿利特水泥凝结时间、抗压强度、电阻率、水化产物组成及微观结构的影响。
3) alinite
阿利尼特
1.
Study on the Early Hydration Product of Alinite Cement;
阿利尼特水泥早期水化产物的研究
2.
By uaing technology of low temperature and salt solution, the author explores the feasibility of sintering the clinker alinite white cement at 12 000 ℃ .
利用低温盐溶工艺 ,探讨在 1 2 0 0℃烧成阿利尼特白水泥熟料的可行性 。
3.
The results show that the optimum burning temperature of the cement is in range of 1200—1350℃ and the composition of cement mineral is alinite with few C 11 A 7·CaCl 2.
研究结果表明 :该白水泥适宜煅烧温度范围为 12 0 0～ 13 5 0℃ ,形成的主要矿物为阿利尼特和少量C1 1 A7·CaCl2 ,随着温度的升高 ,C1 1 A7·CaCl2 逐渐减少 ,在 14 0 0℃ ,阿利尼特开始分解 ,形成了少量的C3S ;在 13 5 0℃下烧成熟料中 ,阿利尼特矿物质为不规则的多面体 ,表面带有平行晶纹 ;熟料为含有大量孔的烧结体 ,烧结体呈三维网络状结构。
4) alite-barium calcium sulphoaluminate cement
阿利特-硫铝酸钡钙水泥
1.
The effects of the composition of clinker minerals,gypsum content and environment temperature on the slurry rheological and dry shrinkage properties of alite-barium calcium sulphoaluminate cement were studied.
结果表明:阿利特—硫铝酸钡钙水泥的新拌浆体属于Bingham型流体,水泥浆体的屈服应力和黏度受熟料中硫铝酸钡钙矿物含量变化的影响较大,随石膏掺量的增加和环境温度的增高而减小;阿利特-硫铝酸钡钙水泥具有一定的微膨胀性能,其砂浆的干缩性能优于硅酸盐水泥砂浆。
2.
Experimental results show that when the slag content is 10% the compressive strength of alite-barium calcium sulphoaluminate cement reachs 44.
研究矿渣掺量对阿利特-硫铝酸钡钙水泥性能的影响,当质量分数掺量为10%时,阿利特-硫铝酸钡钙水泥3 d、28 d的强度分别达到44。
3.
The drying shrinkage and mechanical property of alite-barium calcium sulphoaluminate cement (SABC) mortars were investigated by contrasting with Portland cement mortars.
通过与硅酸盐水泥(portland cement,PC)对比,研究了阿利特-硫铝酸钡钙水泥(alite-barium calcium sulphoaluminate cement,SABC)砂浆的力学性能和干缩性能。
5) alite-sulphoaluminate cement
阿利特-硫铝酸盐水泥
1.
Study of compatibility of superplasticizers with alite-sulphoaluminate cement;
减水剂对阿利特-硫铝酸盐水泥适应性的研究
2.
Effect of mineral composition on adaptability of alite-sulphoaluminate cement with superplasticizer
矿物组成对阿利特-硫铝酸盐水泥与减水剂适应性的影响
3.
The formula of modulus value of alite-sulphoaluminate cement clinker was determined theoretically depending on its mineral composition and requirement for production control.
根据阿利特-硫铝酸盐水泥熟料的矿物组成及生产控制要求,从理论上推导出其率值计算公式。
6) Alite blastfurnace-slag cement
阿利特高炉矿渣水泥