1) manganese tetraoxide
四氧化锰
1.
6 g/cm3 have lower equivalent circulation density(ECD) if manganese tetraoxide is used as the weighting agent,instead of barite.
6 g/cm3以上的加重油基钻井液,用四氧化锰代替重晶石粉加重,能降低钻井液的当量循环密度。
2) hausmannite
四氧化三锰
1.
Kinetics of hausmannite preparation by thermal decomposition of manganese sulfate;
MnSO_4·H_2O热解制备四氧化三锰反应动力学
2.
Nowhausmannite is prepared by electrolyzing manganese metal in our country, thecost of this method is high because of the price of the manganese and the poorof its profitability.
四氧化三锰(Mn_3O_4)是生产软磁铁氧体的重要原料，而铁氧体是一种广泛应用于通信、声像设备、开关电源和磁头工业的软磁材料。
3) Trimanganese tetroxide
四氧化三锰
1.
Preparation of trimanganese tetroxide by air oxidizing free divalent manganese ions;
用空气直接氧化游离二价锰离子制备高纯四氧化三锰
2.
In this paper, the trimanganese tetroxide with high specific surface area was prepared by the oxidation of the manganese powder with the catalyst - ammonium salt,and the effected factors were discussed.
研究了以铵盐作催化剂,利用高纯度锰粉悬浮液通空气催化氧化来制备高比表面四氧化三锰,并讨论了各因素对实验结果的影响,确定了反应的最佳条件;并对产品进行了检测和表征,经XRD检测确定产物为四氧化三锰。
3.
The methods of preparing and measuring of trimanganese tetroxide are introduced in the paper.
介绍了四氧化三锰的制备、检测方法及其相关理论研究 。
4) Mn_3O_4
四氧化三锰
1.
The Calculation and Productive Situation of Mn_3O_4;
我国四氧化三锰生产现状及发展预测
2.
The Current Problems and Countermeasure of the Constant Development of Mn_3O_4 in China;
中国四氧化三锰工业可持续发展面临的问题与对策
3.
Application of Composite Flocculant to Industrial Wastewater Treatment of Mn_3O_4
复合絮凝剂在四氧化三锰工业污水处理中的应用
5) mangano-manganic oxide
四氧化三锰
1.
The basic principle and technological process for producing mangano-manganic oxide from cheap pyrolusite by phase transformation method were introduced.
为了降低四氧化三锰的生产成本,介绍了以价格低廉的软锰矿为原料,使用相转变法制备四氧化三锰的基本原理和工艺过程。
2.
This article introduced production craft type,the characteristic and the profession present siduation oxide,domestic mangano-manganic oxide and showed the development main point in future.
介绍了国内四氧化三锰的生产工艺种类、特点和四氧化三锰的行业现状,说明了今后行业的发展要点。
3.
Powder mangano-manganic oxide is used as adsorbent to deep remove trace molybdenum from manganese sulfate solution.
采用粉体四氧化三锰为吸附剂,对硫酸锰溶液深度除钼工艺进行了研究。
6) manganic manganous oxide
四氧化三锰
1.
A two stage oxidation method to prepare manganic manganous oxide;
两段氧化法制备四氧化三锰
2.
Preparation of manganic manganous oxide control-sample containing sulfur
含硫四氧化三锰控制样品的制备
3.
The manganic manganous oxide is prepared from the purified manganese sulfate solution using hydrogen peroxide as oxidant under alkali medium of ammonia solution.
研究了从软锰矿制备硫酸锰,在碱性溶液中,以过氧化氢为氧化剂,制备高比表面优质四氧化三锰的新工艺。
补充资料：四氧化三锰
分子式：Mn3O4
CAS号：
性质：黑色四方晶系结晶，经灼烧成结晶在温度1443K以下时为扭曲的四方晶系尖晶石结构；1443K以上时则为立方尖晶石结构。在自然界中以黑锰矿形式存在。密度4.856g/cm3。熔点1564℃。可溶于盐酸。不溶于水。在氢气或一氧化碳中加热至高温生成一氧化锰。在氧气中加热生成二氧化锰。高温下碳可使它还原为锰。与盐酸共热可放出氯气并生成二氯化锰。由锰的氧化物或盐类在空气或氧气中于1000℃灼烧制得。或由高纯β-二氧化锰于980～1000℃下焙烧，再经冷却、粉碎制得γ-四氧化三锰。当用二氧化锰或水锰矿为原料时则先焙烧，再在甲烷气体下进一步还原也可制得。主要用于电子工业生产软磁铁氧体，用作电子计算机中存储信息的磁芯、磁盘和磁带，电话用变压器和商品质电感器，电视回归变压器，磁头，电感器，磁放大器，饱和电感器，天线棒等。还可用作某些油漆或涂料的颜料。
CAS号：
性质：黑色四方晶系结晶，经灼烧成结晶在温度1443K以下时为扭曲的四方晶系尖晶石结构；1443K以上时则为立方尖晶石结构。在自然界中以黑锰矿形式存在。密度4.856g/cm3。熔点1564℃。可溶于盐酸。不溶于水。在氢气或一氧化碳中加热至高温生成一氧化锰。在氧气中加热生成二氧化锰。高温下碳可使它还原为锰。与盐酸共热可放出氯气并生成二氯化锰。由锰的氧化物或盐类在空气或氧气中于1000℃灼烧制得。或由高纯β-二氧化锰于980～1000℃下焙烧，再经冷却、粉碎制得γ-四氧化三锰。当用二氧化锰或水锰矿为原料时则先焙烧，再在甲烷气体下进一步还原也可制得。主要用于电子工业生产软磁铁氧体，用作电子计算机中存储信息的磁芯、磁盘和磁带，电话用变压器和商品质电感器，电视回归变压器，磁头，电感器，磁放大器，饱和电感器，天线棒等。还可用作某些油漆或涂料的颜料。