1) Mg-Y-Nd-Zr alloy
Mg-Y-Nd-Zr合金
1.
The deformation behaviors of a kind of Mg-Y-Nd-Zr alloy at temperature range of 300—500℃and strain rate range of 0.
研究了一种Mg-Y-Nd-Zr合金在300—500℃和应变速率为0。
2.
In this paper,homogenizing of ingots of Mg-Y-Nd-Zr alloy at different temperatures and times were carried out.
对Mg-Y-Nd-Zr合金铸锭在不同温度和时间下进行均匀化处理,采用金相显微镜、X射线衍射和扫描电镜及能谱分析仪对合金不同状态下的微观组织和成分进行观察分析。
2) Mg-Y-Nd-Gd-Zr Magnesium Alloy RE-containing
Mg-Y-Nd-Gd-Zr合金
3) Mg-Y-Nd-Zr alloy
Mg-Y-Nd-Zr 合金
1.
In this paper,the experiments of uniform heat treatment at different temperature and time were carried out on the ingots of Mg-Y-Nd-Zr alloy.
本文对 Mg-Y-Nd-Zr 合金铸锭在不同温度和时间下进行均匀化处理,采用金相显微镜、X-Ray 衍射和扫描电镜及能谱分析仪对合金不同状态下的微观组织和成分进行观察分析。
4) Mg-Y-Nd alloy
Mg-Y-Nd合金
1.
The β phase precipitated during ageing Mg-Y-Nd alloy is studied by transmission electron micrscopy.
利用电子显微镜对一种时效后的Mg-Y-Nd合金中析出相(β相)进行了研究。
2.
The compress creep tests of the cast Mg-Y-Nd alloy were carried out at constant stress on Mayes fatigue machine in air.
结果表明:在温度低于300℃、应力低于100 MPa条件下,Mg-Y-Nd合金具有极其优良的蠕变性能,特别是在200℃时,该合金的稳态蠕变速率较Mg-Zn-Ce合金和普通的AZ80,AM60合金降低约3个数量级;滑移和孪生是Mg—Y—Nd合金蠕变变形的基本方式;大量的β相和蠕变期间沉淀相动态析出产生的沉淀强化和晶界强化是提高该合金蠕变抗力的主要机制,MgO质点薄层(在α-Mg/β相界面间)及其独立聚合区(脱离β相)的生成、动态再结晶的发展和初生β相的断裂是降低该合金蠕变抗力的主要原因。
5) Mg-Nd-Zr-Zn alloy
Mg-Nd-Zr-Zn合金
6) Mg-Nd-Zn-Zr cast magnesium alloys
Mg-Nd-Zn-Zr镁合金