The anti-corrosion properties of Cu-Te series alloys in the NH_4Cl solution were studied by the method of immersion testing.
用全浸失重法,研究了碲铜系合金在饱和NH_4Cl溶液中的抗腐蚀性能,结合扫描电镜(SEM)、能谱仪(EDS)等测试方法,初步探讨了合金在饱和NH_4Cl溶液中的腐蚀行为及腐蚀机制,结果表明:碲铜系合金的抗腐蚀性优于纯铜,其腐蚀速率低于纯铜,原因在于碲、镁的加入,可降低纯铜中的非金属杂质含量,同时碲、镁的加入,可沿铜晶界以化合物的形式析出,有利地阻碍了纯铜的沿晶腐蚀。
3) ZnCl_2-NH_4Cl electrolyte
ZnCl_2-NH_4Cl溶液体系
4) saturated solution method
饱和溶液法
1.
METHODS The inclusion compounds were prepared by saturated solution method.
方法采用饱和溶液法制备氟苯尼考-β-环糊精包合物,以包合率和包合物产率为评价指标,筛选最佳包合处方和包合工艺,以差示扫描量热(DSC)分析、溶解度测定和熔点测定等方法对包合物进行确证。
5) supersaturated solution
过饱和溶液
1.
Nucleation process of tetradecyl hydrogen maleate in supersaturated solution;
马来酸氢十四酯(THM)在过饱和溶液中的成核
2.
The calculation of the structural model shows there exist the water-shared ion-pair and the contact ion-pair in the supersaturated solutions.
结构模型的计算表明 ,过饱和溶液中存在着水共享离子对和接触离子对 。
3.
Supersaturated solution of MgO· 3B2O3-H2O was prepared and kept u nder hydrothermal condition at 120 ℃ .
针对中国盐湖硼资源特点,模拟合成MgO·3B2O3-H2O过饱和溶液,在120℃水热条件下对固相析出的过程进行跟踪。
6) CO_2 saturated solution
CO2饱和溶液
补充资料：饱和溶液
| 饱和溶液 saturated solution 在给定温度下，溶质在溶剂中溶解的量达到最大时的溶液。溶质溶于溶剂的溶解过程中，首先是溶质在溶剂中的扩散作用，在溶质表面的分子或离子开始溶解，进而扩散到溶剂中。被溶解了的分子或离子在溶液中不断地运动，当它们和固体表面碰撞时，就有停留在表面上的可能，这种淀积作用是溶解的逆过程。当固体溶质继续溶解，溶液浓度不断增大到某个数值时，淀积和溶解两种作用达成动态平衡状态，即在单位时间内溶解在溶剂中的分子或离子数，和淀积到溶质表面上的分子或离子数相等时，溶解和淀积虽仍在不断地进行，但如果温度不改变，则溶液的浓度已经达到稳定状态，这样的溶液称为饱和溶液，其中所含溶质的量，即该溶质在该温度下的溶解度。由此可见，在饱和溶液中，溶质的溶解速率与它从溶液中淀积的速率相等，处于动态平衡状态。 |
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条