1) NiAl/TiC
TiC/NiAl
3) NiAl-TiC composite coat
NiAl-TiC复合涂层
4) TiC-NiAl composite coating
TiC-NiAl复合涂层
1.
Preparing TiC-NiAl composite coating using electrothermal explosion spraying method;
电热爆炸喷涂法制备TiC-NiAl复合涂层的试验研究
5) NiAI-AI_2O_3-TiC composite
NiAl-Al_2O_3-TiC复合材料
1.
The friction and wear properties of NiAl,NiAl-Cr(Mo)-Hf eutectic alloy and NiAI-AI_2O_3-TiC composite were investigated with an MRH-5A friction and wear tester.
因此NiAl-Al_2O_3-TiC复合材料的抗磨损性能最好,在相同工况下其磨损率为NiAl-Cr(Mo)-Hf共晶合金的1/4-3/4和二元NiAl合金的1/20-1/10。
6) titanium carbide
TiC
1.
The synthesis process of titanium carbide with the detonation wave is investigated.
研究爆轰波条件下合成TiC等碳化物陶瓷粉末的过程。
2.
Results show that the FeNiCr/NiAl-TiC composite coatings are composed of titanium carbide(TiC),intermetallic compound NiAl and ferrite(α-FeNiCr).
用铝热反应合成工艺在钢管内表面制备出了FeNiCr/NiAl-TiC复合涂层。
补充资料：NiAl基金属间化合物高温合金
NiAl基金属间化合物高温合金
NiAl-base intermetallic compound superalloy
N一A IJ一]一nshuJ一an huohewu gaowen heJ旧NIAI基金属间化合物高温合金(NIAI一baseintermetallie eompound superalloy)以NIAI相为基体的金属间化合物高温合金。NIAI合金为体心立方BZ晶体结构.与Ni3AI合金相比，熔点高、密度小、具有更好的抗氧化性。但用作高温结构材料有两点不足:抗高温蠕变性能太差;室温脆性尚未得到根本解决。提高强度主要通过添加高熔点合金元素的固溶强化或者第二相质点的弥散强化(见高温合金强化)。添加铁可以形成两相组织，能提高屈服强度。通过机械合金化工艺加入第二相质点(Y刃3，TIBZ)也可以提高强度。最近，改善塑性的研究已得到令人鼓舞的结果，通过调整含铝量使之偏离正常成分而处在亚当量范围，获得y+丫两相组织(见高温合金材料的金属间化合物相)，可使N;AI基金属间化合物高温合金的室温拉伸塑性提高到5%~6%。 (邹敦叙)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。