1) glass infiltrated alumina ceramics
玻璃渗透氧化铝陶瓷
1.
The fabrication process of glass infiltrated alumina ceramics(in-ceram alumina) was investigated,such as changing powder/liquid ratio,pre-sintered temperature and forming method.
通过改变氧化铝粉浆的粉液比、预烧温度以及成型工艺等参数,研究了以上因素对用于制作全瓷冠桥的In-Ceram玻璃渗透氧化铝陶瓷复合体性能的影响。
2.
The fabrication process of glass infiltrated alumina ceramics (CAD/CAM&In-ceram alumina),such as solid loading,presintered temperature and forming method,was investigated.
研究了氧化铝粉浆的固相含量及预烧温度、氧化铝基底块体成形工艺对用于制作全瓷冠桥的计算机辅助设计/加工(CAD/CAM)&In-Ceram玻璃渗透氧化铝陶瓷复合体性能的影响。
2) alumina glass-infiltrated ceramic
氧化铝玻璃渗透陶瓷
3) alumina glass-infiltrated composite
氧化铝渗透陶瓷
1.
Effects of veneering porcelain in different color on CAD/CAM alumina glass-infiltrated composite appearance;
不同颜色饰面瓷对CAD/CAM氧化铝渗透陶瓷颜色的影响
5) glass infiltrated ceramic
玻璃渗透陶瓷
1.
Study on fracture toughness of glass infiltrated ceramic inner crown;
氧化铝玻璃渗透陶瓷底层冠强度的研究
6) transparent oxyfluoride glass ceramic
透明氟氧化物玻璃陶瓷
1.
In this paper,we reported the spectroscopic properties of praseodymium ions(Pr~(3+)) doped transparent oxyfluoride glass ceramic excited with different laser lines,such as 532,514.
5 nm,研究稀土Pr3+掺杂的透明氟氧化物玻璃陶瓷中Pr3+在LaF3微晶环境和玻璃环境中的不同的荧光行为。
补充资料：氧化铝生物陶瓷
分子式：
CAS号：
性质：由高纯度(>99.5％)α-氧化铝构成的一种近于惰性的生物陶瓷，亦称纯刚玉生物陶瓷材料。它在生物环境中不被腐蚀或溶解，致密型陶瓷和组织间的结合是形态结合，多孔型陶瓷与组织间的结合是生物结合。两者植入骨内时均要求与原骨紧密的配合，否则会因界面松动或在界面处切断长入孔隙内的组织而使植入失败。它还可用作牙种植体、耳听骨修复体、骨螺钉和药物释放载体等。因其弹性模量远高于自然骨，拉伸强度低，易发生老化和疲劳破坏，故不宜用作承受复杂应力的骨替换材料。
CAS号：
性质：由高纯度(>99.5％)α-氧化铝构成的一种近于惰性的生物陶瓷，亦称纯刚玉生物陶瓷材料。它在生物环境中不被腐蚀或溶解，致密型陶瓷和组织间的结合是形态结合，多孔型陶瓷与组织间的结合是生物结合。两者植入骨内时均要求与原骨紧密的配合，否则会因界面松动或在界面处切断长入孔隙内的组织而使植入失败。它还可用作牙种植体、耳听骨修复体、骨螺钉和药物释放载体等。因其弹性模量远高于自然骨，拉伸强度低，易发生老化和疲劳破坏，故不宜用作承受复杂应力的骨替换材料。