While the Co3O4,transition-metal oxides(V2O5,Ta2O5,MoO3 and TiO2) and carbon black was the raw materials,ultrafine Co-inhibitor composite powders(Co-VC,Co-TaC,Co-Mo2C and Co-TiC),which can be applied in hardmetal industry,were synthesized via direct reduction & carbonization process in vacuum.

以氧化钴(Co3O4)、过渡金属氧化物(V2O5、Ta2O5、MoO3、TiO2)和碳粉(C)为原料,用真空直接还原碳化技术制备了应用于硬质合金的钴-抑制剂(Co-VC、Co-TaC、Co-Mo2C、Co-TiC)超细复合粉末。

Nano-composite WC-Co powder was synthesized by direct reduction & carbonization process. 点击朗读

用直接还原碳化法制备了纳米复合WC-Co粉末。

更多例句>>

2) CDRM

碳粉直接还原法

3) direct reduction 点击朗读

直接还原

Producing iron nuggets with direct reduction from coal mixed pellets; 点击朗读

内配煤团块直接还原法制备铁粒技术研究

One-step process for direct reduction of Xinjiang magnetite concentrate; 点击朗读

一步法直接还原新疆磁铁精矿

Experimental investigation of direct reduction of Brazil Carajas iron-rich hematite fines;

巴西赤铁矿富矿粉直接还原试验研究

更多例句>>

4) reduction/carbonization 点击朗读

还原/碳化

Dissolving ammonium vanadate(NH_4VO_3)and nanometer carbon in de-ionized water,the precursor powder was obtained through heating and drying,and nanometer vanadium carbide was prepared through reduction/carbonization of the precursor powder.

将偏钒酸铵和纳米碳黑溶于去离子水中,通过加热、干燥后制得前驱体粉末,将前驱体粉末还原/碳化后得到纳米V_8C_7粉末。

5) reduction carbonization 点击朗读

还原碳化

The constitutes of theoretic power consumption in BF slag reduction carbonization of Pangang are analysed,and the theoretic value of the power consumption is compared with the real one.

分析了攀钢高炉渣还原碳化的理论电耗构成,并与实际情况进行了对比,找到了造成电耗高的原因,指出“合理利用”从高炉排出的熔融高炉渣的显热、改善冶炼动力学条件、提高电炉的热效率是降低电耗的3个主要途径,同时还应从理论上深入研究电炉冶炼条件下的相关机理和理论,才能解决经济可行性问题。

更多例句>>

6) direct reduced iron 点击朗读

直接还原铁直接还原铁

例句>>

补充资料：直接还原度

直接还原度
degree of direct reduction

zh一J ie huanyandu直接还原度(degree of direet reduetion)高炉内直接还原发展的程度，是衡量高炉能量利用的重要指标。在高炉铁矿石还原过程中凡直接消耗碳产生CO的和参与COZ+C一2C0的反应，本质上都与铁的直接还原类似，都发生在高温区，并吸收热量，使风口前燃烧碳量减少、焦比增高。表示方法直接还原度有铁的直接还原度和高炉直接还原度两种表示方法。铁的直接还原度从FeO中以直接还原方式得到的铁量与全部还原出来的铁量之比值(rd)。它是由前苏联巴甫洛夫 (M.A.naB二B)定义的。他认为高炉内FeZO3~Fe3O4~FeO全部由间接还原完成，从FeO还原到金蒸鞭撇鬓{ 属铁一部分靠CO、H:的间接还原，其余则靠碳的直接还原度。还原，Feco riCo一瓦万 ~56f‘还一~~C‘一哭 ___互里生_旦】二旦当垫迪逻_竺竺‘卫卫式中Feco是从FeO中用co间榕还原的铁量，k创t Fe还0~FeFe还铁，式中Fe二为直接还原与间接还原两种方式还原出来__。八._。八，、.‘一。，J~~一~J.二，~，/J、r·，、。~一~叫/卜_56一_co，12 CO、性、勘的总铁量;Fed为直接还原的铁量;0、为直接还原各种Feco一嚣(C氧己瓦.城)稼砰丽夏一兰二二履立性男元素夺取的氧量;odsi.Mn，P直接还原非铁元素夺取的氧12Fe刃，12Mn0，、量;OFe、Fe由FeO还原到Fe时夺取的全部氧量;Cd、16087 直接还原铁消耗的碳量。直接还原度与间接还原度的C02璐+挥)、Fe20。、MnO，分别为冶炼h生铁由熔剂、焦总和为1。也即相应的间接还原度，1一1一:d一Fe;/炭挥发分中带入的COZ、由炉料带入的Fe203(应扣除 Fe示在冶炼条件基本稳定的情况下，铁的直接还原度被H:还原生成Feo的部分)和MnoZ的量，kg/t铁; 能较灵敏地反映高炉还原过程的变化。。丝目_、_ ~~t扮一甲介竺’二’，、_一丫贡.寸胜仓「厂’_，__二、__FeH，万nZ还高炉直接还原度高炉内氧化物(除FeO外尚有r峡一斌一命诬了“ 5102、MnO、PZOS，以及微量元素Nb、Cr、V、Ti等的氧、、。曰、，，、，、;、，且，，、二二。，。2、1v，11?、i:?。，从~，二，。

说明：补充资料仅用于学习参考，请勿用于其它任何用途。

参考词条

流化床铁矿石直接还原直接碳化原位还原碳化直接还原机理气基直接还原

直接还原铁直接还原(DR) 直接电还原还原直接黑直接还原度

说明：双击或选中下面任意单词，将显示该词的音标、读音、翻译等；选中中文或多个词，将显示翻译。
	您的位置：首页 -> 词典 -> 直接还原碳化 1) direct reduction & carbonization 直接还原碳化 1. While the Co3O4,transition-metal oxides(V2O5,Ta2O5,MoO3 and TiO2) and carbon black was the raw materials,ultrafine Co-inhibitor composite powders(Co-VC,Co-TaC,Co-Mo2C and Co-TiC),which can be applied in hardmetal industry,were synthesized via direct reduction & carbonization process in vacuum. 以氧化钴(Co3O4)、过渡金属氧化物(V2O5、Ta2O5、MoO3、TiO2)和碳粉(C)为原料,用真空直接还原碳化技术制备了应用于硬质合金的钴-抑制剂(Co-VC、Co-TaC、Co-Mo2C、Co-TiC)超细复合粉末。 2. Nano-composite WC-Co powder was synthesized by direct reduction & carbonization process. 用直接还原碳化法制备了纳米复合WC-Co粉末。更多例句>> 2) CDRM 碳粉直接还原法 3) direct reduction 直接还原 1. Producing iron nuggets with direct reduction from coal mixed pellets; 内配煤团块直接还原法制备铁粒技术研究 2. One-step process for direct reduction of Xinjiang magnetite concentrate; 一步法直接还原新疆磁铁精矿 3. Experimental investigation of direct reduction of Brazil Carajas iron-rich hematite fines; 巴西赤铁矿富矿粉直接还原试验研究更多例句>> 4) reduction/carbonization 还原/碳化 1. Dissolving ammonium vanadate(NH_4VO_3)and nanometer carbon in de-ionized water,the precursor powder was obtained through heating and drying,and nanometer vanadium carbide was prepared through reduction/carbonization of the precursor powder. 将偏钒酸铵和纳米碳黑溶于去离子水中,通过加热、干燥后制得前驱体粉末,将前驱体粉末还原/碳化后得到纳米V_8C_7粉末。 5) reduction carbonization 还原碳化 1. The constitutes of theoretic power consumption in BF slag reduction carbonization of Pangang are analysed,and the theoretic value of the power consumption is compared with the real one. 分析了攀钢高炉渣还原碳化的理论电耗构成,并与实际情况进行了对比,找到了造成电耗高的原因,指出“合理利用”从高炉排出的熔融高炉渣的显热、改善冶炼动力学条件、提高电炉的热效率是降低电耗的3个主要途径,同时还应从理论上深入研究电炉冶炼条件下的相关机理和理论,才能解决经济可行性问题。更多例句>> 6) direct reduced iron 直接还原铁直接还原铁例句>> 补充资料：直接还原度直接还原度 degree of direct reduction zh一J ie huanyandu直接还原度(degree of direet reduetion)高炉内直接还原发展的程度，是衡量高炉能量利用的重要指标。在高炉铁矿石还原过程中凡直接消耗碳产生CO的和参与COZ+C一2C0的反应，本质上都与铁的直接还原类似，都发生在高温区，并吸收热量，使风口前燃烧碳量减少、焦比增高。表示方法直接还原度有铁的直接还原度和高炉直接还原度两种表示方法。铁的直接还原度从FeO中以直接还原方式得到的铁量与全部还原出来的铁量之比值(rd)。它是由前苏联巴甫洛夫 (M.A.naB二B)定义的。他认为高炉内FeZO3~Fe3O4~FeO全部由间接还原完成，从FeO还原到金蒸鞭撇鬓{ 属铁一部分靠CO、H:的间接还原，其余则靠碳的直接还原度。还原，Feco riCo一瓦万 ~56f‘还一~~C‘一哭 ___互里生_旦】二旦当垫迪逻_竺竺‘卫卫式中Feco是从FeO中用co间榕还原的铁量，k创t Fe还0~FeFe还铁，式中Fe二为直接还原与间接还原两种方式还原出来__。八._。八，、.‘一。，J~~一~J.二，~，/J、r·，、。~一~叫/卜_56一_co，12 CO、性、勘的总铁量;Fed为直接还原的铁量;0、为直接还原各种Feco一嚣(C氧己瓦.城)稼砰丽夏一兰二二履立性男元素夺取的氧量;odsi.Mn，P直接还原非铁元素夺取的氧12Fe刃，12Mn0，、量;OFe、Fe由FeO还原到Fe时夺取的全部氧量;Cd、16087 直接还原铁消耗的碳量。直接还原度与间接还原度的C02璐+挥)、Fe20。、MnO，分别为冶炼h生铁由熔剂、焦总和为1。也即相应的间接还原度，1一1一:d一Fe;/炭挥发分中带入的COZ、由炉料带入的Fe203(应扣除 Fe示在冶炼条件基本稳定的情况下，铁的直接还原度被H:还原生成Feo的部分)和MnoZ的量，kg/t铁; 能较灵敏地反映高炉还原过程的变化。。丝目_、_ ~~t扮一甲介竺’二’，、_一丫贡.寸胜仓「厂’_，__二、__FeH，万nZ还高炉直接还原度高炉内氧化物(除FeO外尚有r峡一斌一命诬了“ 5102、MnO、PZOS，以及微量元素Nb、Cr、V、Ti等的氧、、。曰、，，、，、;、，且，，、二二。，。2、1v，11?、i:?。，从~，二，。说明：补充资料仅用于学习参考，请勿用于其它任何用途。参考词条流化床铁矿石直接还原直接碳化原位还原碳化直接还原机理气基直接还原

©2011 dictall.com