1) alumina sol-mixed method
氧化铝溶胶混合法
2) alumina sol
氧化铝溶胶
1.
Al2O3 ceramic coatings were prepared on mild steel substrates with alumina sol as precursor by electrophoretic deposition and low-temperature sintering.
以氧化铝溶胶为前驱体,采用电泳沉积和低温煅烧法在低碳钢基体上制备了氧化铝陶瓷涂层,并对其成分、表面形貌及耐蚀性进行了研究。
2.
In order to reduce the ratio of the anode oxidation and excessive anode consumption,the writer puts forward a method that the relatively compact alumina coatings(film),alumina sol as the basic cohere component, is prepared on carbon anode surface by original located solidification.
提出采用在炭素阳极表面原位固化制备以氧化铝溶胶为基本粘结相、相对致密的氧化铝涂层(膜)的方法,达到减少阳极氧化、降低阳极过量消耗的目的。
3.
Based on the infrared anomalous dispersion of compact alumina film, the character of alumina sols and the processing for fabricating compact alumina film were studied by using sol-gel method.
本文基于致密氧化铝膜的红外反常色散特性，结合溶胶-凝胶技术，采用浸渍提拉法、旋覆法和电泳沉积工艺，对氧化铝溶胶的性质和致密氧化铝膜的制备工艺进行了研究。
3) uranium mixed-oxide sol
钍-铀混合氧化物溶胶
4) aluminium hydroxide sol
氢氧化铝溶胶
1.
Study on preparing stable aluminium hydroxide sol through aluminium by nitric acid;
纯铝制备稳定氢氧化铝溶胶的研究
5) Nano-scaled Al_2O_3 sol
纳米氧化铝溶胶
6) γ-alumina sol
γ-氧化铝溶胶
补充资料：溶胶-凝胶法
分子式：
CAS号：
性质：一种用于制取无机固体材料和器件的方法。无机固体化合物和无机材料通常是利用高温固相反应制备，但是，一般地说，高温固相反应得到固体产物的均匀性较差，反应所需的温度较高，产物的料理论基础和形貌也无法控制。溶胶-凝胶方法利用前体物（如醇盐或无机盐）将反应物在分子的尺度上均匀混合，经溶胶和凝胶过程使之转变为固体；由于固体凝胶中反应物是在分子水平上均匀混合，避免了固相反应扩散过程，使反应可以在较低的温度下进行，还可以根据需要将凝胶成型，再经热处理得到具有一定形状的材料和器件。利用溶胶-凝胶方法可以制备出各种形态的材料，如薄膜、纤维、块体或粉末等。近年来，溶胶-凝胶方法在很多领域中得到了广泛应用，特别是在陶瓷材料和器件上制造中的应用，得到了多种均匀、具有特定微结构和性能的固体材料。
CAS号：
性质：一种用于制取无机固体材料和器件的方法。无机固体化合物和无机材料通常是利用高温固相反应制备，但是，一般地说，高温固相反应得到固体产物的均匀性较差，反应所需的温度较高，产物的料理论基础和形貌也无法控制。溶胶-凝胶方法利用前体物（如醇盐或无机盐）将反应物在分子的尺度上均匀混合，经溶胶和凝胶过程使之转变为固体；由于固体凝胶中反应物是在分子水平上均匀混合，避免了固相反应扩散过程，使反应可以在较低的温度下进行，还可以根据需要将凝胶成型，再经热处理得到具有一定形状的材料和器件。利用溶胶-凝胶方法可以制备出各种形态的材料，如薄膜、纤维、块体或粉末等。近年来，溶胶-凝胶方法在很多领域中得到了广泛应用，特别是在陶瓷材料和器件上制造中的应用，得到了多种均匀、具有特定微结构和性能的固体材料。