T-剥离强度,T-style peel strength,在线英语词典,英文翻译,专业英语

1) T-style peel strength

T-剥离强度

At the same time,the effects of EDA contents and addition sequence on the T-style peel strength,particle size,viscosity,water absorption,and the glass transition temperature(Tg)of the waterborne polyurethane adhesives were also studied.

以聚酯多元醇、聚醚多元醇、甲苯二异氰酸酯(TDI)、二羟甲基丙酸(DMPA)、乙二胺(EDA)等为主要原料合成了水性聚氨酯乳液(WPU),考察了EDA不同用量和加料顺序对水性聚氨酯胶粘剂的T-剥离强度、粒径、粘度、耐水性、玻璃化转变温度(Tg)等性能的影响。

2) T-style peel strength

T剥离强度

The effects of the content of carboxyl(COOH%),the mol ratio of-NCO and-OH(R Value),and the content of crosslinker on the properties of aqueous Polyurethane(PU) and T-style peel strength were discussed,and thus a kind of modified inner crosslinking aqueous polyurethane adhesive was synthesized.

通过改变羧基含量(COOH%)、异氰酸酯基(-NCO)与羟基(-OH)的摩尔比(R值)、交联剂用量,考察了它们对聚氨酯乳液的粘度、胶膜的耐水性及复合薄膜T剥离强度的影响,合成了一种内交联型复合薄膜用水性聚氨酯胶粘剂。

It was found that T-Style peel strength dropped when content of butyl acrylate increased.

以PUA乳液作为复合薄膜胶粘剂时，发现随着BA含量的增加，复合薄膜的T剥离强度明显降低。

3) t-T

t-T

Objective To study the clinical effect of T wave transient change(T wave change from upright to inversion,then upright again,t-T)by routine12leads of electrocardiogram.

目的:通过常规12导联心电图研究一过性T波变化(即T波由直立变为倒置再直立,简称t-T)的临床意义。

4) T/T

T/T

5) T-T absorption

T-T吸收

6) T H1 /T H2

T_（H1）T_（H2）

参考词条

T-T势 t-t-'t-″J-U模型 t-t'-t″-J模型 T-box express in T cell（T-bet） t-t'-t-J模型 t-BN T型 T酸 T-Hg T-P T-RFLP T[O] t-BAMBP T恤 CCSD（T）二级学院办学自主权

补充资料：剥离强度试验

分子式：
CAS号：

性质：测定橡胶与金属或织物黏合面之间黏合强度的一种试验，简称剥离试验，也称密着力试验。试验时规定试样有效宽度为10mm，25mm，50mm，有效剥离长度70mm，剥离速度100mm/min±5mm/min，标准剥离角度为90°，180°两种，橡胶与金属或织物的剥离强度按下式计算。，式中，σ_b为橡胶与金属粘接的剥离强度，kN/m；S为有效剥离长度内所记录图形面积，cm2或m2；B为试样宽度，cm或m；C为剥离曲线上负荷坐标单位长度所代表的负荷，kgf/cm或kN/m；L为有效剥离长度，cm。对橡胶与织物剥离强度也可以按剥离曲线中部50％区域内从小到大排列的峰值中，取前一半较小峰值的平均值作为试样的剥离强度。该方法可用于质量控制或对黏合体系的比较，但也可引伸到研究试样大小、剥离角度、试验速度等对试验结果的影响。

说明：补充资料仅用于学习参考，请勿用于其它任何用途。

首页 \| 翻译 \| 影视 \| 论坛 \| 索引 T-T湮灭 T-T湮没 P-T-t T-T淬灭 T/T（电汇）

1) T-style peel strength T-剥离强度 1. At the same time,the effects of EDA contents and addition sequence on the T-style peel strength,particle size,viscosity,water absorption,and the glass transition temperature(Tg)of the waterborne polyurethane adhesives were also studied. 以聚酯多元醇、聚醚多元醇、甲苯二异氰酸酯(TDI)、二羟甲基丙酸(DMPA)、乙二胺(EDA)等为主要原料合成了水性聚氨酯乳液(WPU),考察了EDA不同用量和加料顺序对水性聚氨酯胶粘剂的T-剥离强度、粒径、粘度、耐水性、玻璃化转变温度(Tg)等性能的影响。 2) T-style peel strength T剥离强度 1. The effects of the content of carboxyl(COOH%),the mol ratio of-NCO and-OH(R Value),and the content of crosslinker on the properties of aqueous Polyurethane(PU) and T-style peel strength were discussed,and thus a kind of modified inner crosslinking aqueous polyurethane adhesive was synthesized. 通过改变羧基含量(COOH%)、异氰酸酯基(-NCO)与羟基(-OH)的摩尔比(R值)、交联剂用量,考察了它们对聚氨酯乳液的粘度、胶膜的耐水性及复合薄膜T剥离强度的影响,合成了一种内交联型复合薄膜用水性聚氨酯胶粘剂。 2. It was found that T-Style peel strength dropped when content of butyl acrylate increased. 以PUA乳液作为复合薄膜胶粘剂时，发现随着BA含量的增加，复合薄膜的T剥离强度明显降低。 3) t-T t-T 1. Objective To study the clinical effect of T wave transient change(T wave change from upright to inversion,then upright again,t-T)by routine12leads of electrocardiogram. 目的:通过常规12导联心电图研究一过性T波变化(即T波由直立变为倒置再直立,简称t-T)的临床意义。 4) T/T T/T 5) T-T absorption T-T吸收 6) T H1 /T H2 T_（H1）T_（H2）参考词条 T-T势 t-t-'t-″J-U模型 t-t'-t″-J模型 T-box express in T cell（T-bet） t-t'-t-J模型 t-BN T型 T酸 T-Hg T-P T-RFLP T[O] t-BAMBP T恤 CCSD（T）二级学院办学自主权补充资料：剥离强度试验分子式： CAS号：性质：测定橡胶与金属或织物黏合面之间黏合强度的一种试验，简称剥离试验，也称密着力试验。试验时规定试样有效宽度为10mm，25mm，50mm，有效剥离长度70mm，剥离速度100mm/min±5mm/min，标准剥离角度为90°，180°两种，橡胶与金属或织物的剥离强度按下式计算。，式中，σ_b为橡胶与金属粘接的剥离强度，kN/m；S为有效剥离长度内所记录图形面积，cm2或m2；B为试样宽度，cm或m；C为剥离曲线上负荷坐标单位长度所代表的负荷，kgf/cm或kN/m；L为有效剥离长度，cm。对橡胶与织物剥离强度也可以按剥离曲线中部50％区域内从小到大排列的峰值中，取前一半较小峰值的平均值作为试样的剥离强度。该方法可用于质量控制或对黏合体系的比较，但也可引伸到研究试样大小、剥离角度、试验速度等对试验结果的影响。说明：补充资料仅用于学习参考，请勿用于其它任何用途。