1) Abnormal solidification eutectic
非正常共晶凝固组织
3) Microstructure of abnormal normalizing
非正常正火组织
4) non-equilibrium solidification microstructure
非平衡凝固组织
5) eutectic solidification
共晶凝固
1.
The crystal growth process with Bridgman method was simulated via NH4Cl-H2O solution eutectic solidification.
利用NH4Cl-H2O溶液的共晶凝固模拟Bridgman法晶体生长过程,通过粒子图像测速系统测量了矩形腔和圆柱腔内NH4Cl-H2O溶液共晶凝固过程中的流场,结合温度变化得到了凝固过程中流动和温度的耦合规律。
2.
The droplet velocity,size distribution,and the procedures of droplet cooling,recalescence,segregated solidification,eutectic solidification and liquid solidification are analyzed.
文章分析了雾化凝固过程中的液滴的速度与粒度分布及液态冷却、再辉、偏析凝固、共晶凝固与液态凝固阶段,通过对合金液滴凝固过程中凝固潜热的释放与环境导热的分析导出了不同阶段液滴温度变化方程。
3.
Thermal analysis and micro/macro-structure observation were employed to investigate the effect of addition of misch metal(MM)on eutectic solidification of Al-13%Si alloy modified with strontium.
采用热分析技术与组织观察研究了混合稀土(MM)加入对Sr变质Al-13%Si合金共晶凝固的影响。
6) non-equilibrium freezing eutectic
非平衡凝固共晶体
1.
The results showed that non-equilibrium freezing eutectic containing Al,Zn,Mg,Cu in the ingot not only dissolves into the alloy matrix,but also transforms into S .
结果表明:在均匀化处理过程中,铸锭中含有Al,Zn,Mg,Cu元素的非平衡凝固共晶体在向合金基体溶解的同时还转变形成S相(Al2CuMg),形成的S相在该合金中的熔化温度为490℃;均匀化处理初期,含有Al,Zn,Mg,Cu的非平衡凝固共晶体转变成S相的速度大于S相向合金基体溶解的速度,导致S相数量随均匀化处理时间的延长,先增加随后减少到平衡值,但不能全部溶入合金基体。
补充资料：共晶凝固
eutecticsolidification：熔态合金转变为共晶体的凝固过程。二元合金的共晶凝固是在恒温下进行的；三元合金的共晶凝固则是在一个温度区间进行的。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。