1) cationic dispersed rosin size
阳离子分散松香胶
1.
Application of the cationic dispersed rosin size made in lab in the neutral papermaking system;
自制阳离子分散松香胶在中性抄纸中的应用
2.
As a new internal sizing agent, cationic dispersed rosin size has many advantages.
阳离子分散松香胶作为新型浆内施胶剂,因具有自行留着在纤维表面、可减少硫酸铝用量、适用于二次纤维纸浆等优势而引起造纸工作者极大的关注。
3.
Certain polymeric substances can be effectively used as efficient emulsifying and dispersing agents for the preparation of cationic dispersed rosin sizes.
对于阳离子分散松香胶的制备而言,聚合物类物质在特定的条件下可用作有效的乳化与分散剂。
2) cationic rosin size
阳离子分散松香胶
1.
Rosin extenders and mordants were the research highlights of this paper in order to improve the sizing efficiency of cationic rosin size.
本论文是围绕着提高阳离子分散松香胶施胶性能而对松香补充剂及松香施胶媒介物质进行的研究。
2.
C_5 petroleum resin was co-emulsified with rosin by a cationic complex emulsifying system to prepare cationic rosin size.
采用C_5石油树脂做松香补充剂,利用阳离子复配型乳化剂制备阳离子分散松香胶,初步探讨C_5石油树脂在胶料中的含量、硫酸铝用量、施胶剂用量对其施胶效果的影响。
3.
The effects of dosages of cationic rosin sizes,AZC and alum sulfate,as well as the proportion of them were investigated.
利用实验室自制的阳离子分散松香胶,与碳酸锆铵一起对纸张进行浸渍施胶,利用碳酸锆铵与松香羧基之间的反应,研究碳酸锆铵对阳离子分散松香胶的施胶促进作用。
3) cationic rosin emulsion
阳离子分散松香施胶剂
1.
The promoting effects of a cationic styrene/butyl acrylate copolymer emulsion on the sizing efficacy of a cationic rosin emulsion were investigated on a pulp containing 10% of CaCO3.
考察了阳离子型苯丙乳液在含质量分数为10%的碳酸钙抄纸体系中对阳离子分散松香施胶剂的增效作用。
4) cationic dispersed wax-rosin size
阳离子分散石蜡松香胶
1.
The preparation and application of cationic dispersed wax-rosin size were investigated in our work.
针对阳离子分散石蜡松香胶的制备与应用进行了研究与探讨,相关实验结果表明,由十六烷基三甲基溴化铵、十二烷基二甲基苄基氯化铵、烷基酚聚氧乙烯醚、山梨醇酐单油酸酯、聚氧乙烯失水山梨醇单油酸酯及脂肪醇聚氧乙烯醚构成的低分子表面活性剂复配体系不能有效地用于阳离子分散石蜡松香胶的制备;由常规阳离子水溶性聚合物与低分子表面活性剂构成的复配体系可在特定的条件下对松香/石蜡混合物起到良好的乳化与分散作用,但低分子表面活性剂用量大(被乳化物质量的20%及以上),胶料在纸料质量的1·0%及以下的用量范围内施胶效果具有局限性;由自制阳离子共聚物型有机微粒与低分子表面活性剂构成的复合乳化与分散体系可有效地用于阳离子分散石蜡松香胶的制备,该体系的有效性很可能得益于独特的有机微粒及胶料粒子特征,低分子表面活性剂用量可降低至被乳化物质量的3·0%,所得胶料在纸料质量的0。
5) microparticle-emulsified cationic dispersed rosin size
阳离子微粒乳化中性分散松香胶
1.
According to the experimental results,the optimum emulsifying temperature and adding time in the preparation process of microparticle-emulsified cationic dispersed rosin size were 140℃ and 20min,respectively.
采用常压逆转工艺制备出了性能优良的阳离子微粒乳化中性分散松香胶,对制备过程中乳化温度、复合乳化剂的加入时间进行了探讨,实验结果表明,在综合考虑操作成本与乳化效果的前提下,乳化温度以140℃为宜,复合乳化剂的加入时间以20m in为宜。
6) anionic dispersed rosin size
阴离子分散松香胶
1.
Neutral sizing with anionic dispersed rosin size and polyaluminium chloride was studied． It was shown that sizing was apparently affected by the quality and dosage of anionic dispersed rosin size，the species and charge of polyaluminium chloride and filler，the pH value of stock and wet－end additives as well as by some basic technical factors
重点对以阴离子分散松香胶和聚合氯化铝组成的松香中性施胶体系的施胶特性进行了研究。
补充资料：分散型阳离子艳蓝RL
分子式：
CAS号：
性质：深蓝色粉末或液体。染色速度缓慢，容易匀染，透染性好。对染液pH值不敏感。在低温(常温-80℃左右)与其他类染料和助剂同浴时不产生沉淀。阳离子艳蓝RL与1-萘磺酸反应成盐，经过滤，干燥而得。用于腈纶染色，以及涤/腈混纺织物一浴法的染色。
CAS号：
性质：深蓝色粉末或液体。染色速度缓慢，容易匀染，透染性好。对染液pH值不敏感。在低温(常温-80℃左右)与其他类染料和助剂同浴时不产生沉淀。阳离子艳蓝RL与1-萘磺酸反应成盐，经过滤，干燥而得。用于腈纶染色，以及涤/腈混纺织物一浴法的染色。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条