1) Slag system
渣系
1.
It is introduced the practice to prolong the work life of converter for smelting vanadium-titanium molten-iron with adopting twin process, improving bricking, implementing one-time success drawing tapping, lowering tapping temperature, reforming slag system, improving slag-splashing furnace protecting effect.
介绍了承钢采用双联工艺,在用含钒钛铁水炼钢生产过程中通过改进砌炉工艺、执行一次拉成出钢操作、降低出钢温度、改造渣系、提高溅渣护炉效果等措施的实施大幅度提高转炉炉龄。
2.
The effect of slag systems and welding parameters on arc shape and droplet transfer behavior of flux cored arc welding (FCAW) in carbon dioxide protective atmosphere was studied on the basis of digital camera technology.
基于数码照相技术研究了CO2保护气氛下,渣系和焊接参数对药芯焊丝电弧焊(FCAW)电弧形态和熔滴过渡行为的影响。
3.
Aimed at problems in present research and application of flux-cored wires, the peculiar phenomenon-lagging melting phenomena in FCAW of using carbon dioxide as protective atmosphere was studied by digital camera technology from three factors-the type of slag system,welding parameter and sections of flux-cored wires.
针对当前药芯焊丝应用及研究中存在的问题 ,用数码照相技术研究了CO2 保护气氛下药芯焊丝电弧焊所特有的“滞熔”现象 ,主要从药芯焊丝渣系、焊接参数、焊丝截面方面对“滞熔”形成原因进行了探讨。
2) slag
[英][slæɡ] [美][slæg]
渣系
1.
The article has described the melting process,refining slag,vacuum degree,vacuum holding time,weak argon blowing time and ingot mold temperature that might affect the quality of the bearing steel.
研究了初炼炉冶炼工艺、精炼渣系、真空度、真空保持时间、弱吹氩时间、钢锭模温度对轴承钢质量的影响,结果表明,合适的炉渣碱度、真空度≤30 Pa,真空保持时间≥15 min,弱吹氩≥8 min,保证钢锭模温度在30~100℃,可以生产出氧含量、夹杂物含量低及表面质量良好的轴承钢。
2.
In this paper with the trait of oxidation dephosphorization and the requirement of ultra-low phosphorus steel in bao steel we have studied three types of dephosphorization slags and effection of technology.
本文根据氧化脱磷的特点和宝钢超低磷钢生产的实际需要,以确定低磷钢水炉外深脱磷所需合理脱磷剂和脱磷效果为目标,以管线钢为实验钢种研究了三大渣系脱磷剂及工艺因素对脱磷效果的影响。
3.
By adopting two kinds of slags with different electric resistance,the W6Mo5Cr4V2 steel electroslag remelting test has been operated.
采用两种不同电阻率的渣系进行电渣重熔W6Mo5Cr4V2钢实验。
3) refining slag
精炼渣系
1.
Factors related to increase ot Al content such as refining slag compositions,molten steel composition LF refining time etc.
通过理论计算和工业生产实践研究了不同的渣系、钢水成分、处理时间等对LF精炼过程增铝的影响,不同精炼渣系下钢中夹杂的组成,结果表明采用CaO-SiO2渣系LF处理过程几乎不发生增铝现象,而采用CaO-Al2O3渣系随着处理时间的延长以及钢种成分的区别,钢中铝有不同程度的增加,生产实践结果与理论计算趋势基本一致。
2.
The desulfurization effect for both CaO-Al2O3-MgO-SiO2 and CaO-Al2O3-MgO-SiO2-CaF2 refining slag are studied in ladle furnace process.
在钢包精炼炉上对CaO-Al2O3-MgO-SiO2和CaO-Al2O3-MgO-SiO2-CaF2两种精炼渣系的脱硫效果进行了研究。
5) slag transportation system
运渣系统
6) slag sluicing system
渣水系统
1.
Studies were made to improve the bin structure and optimize the design of slag sluicing system, such as changed the supporting frame, platform and clarifier with steel reinforced concrete structure, removed the decanting element in the process, modified the arrangement of the decanting tubes, changed the.
针对脱水仓在运行中暴露出的设备结构不合理、腐蚀、磨损等问题,对其进行完善脱水仓结构和优化渣水系统设计方面的改进,包括钢结构支撑框架、平台和水池改为钢筋混凝土结构,拆除中间析水元件,修改析水管的布置,将底部析水元件气动排水阀改为手动阀,改脱渣水直接排放为闭式循环等。
补充资料：电渣重熔渣系
电渣重熔渣系
slags electroslag remelting
d ianzha ehongrong Zhox，电渣重熔渣系(slags eleetroslag remelting) 含有CaO、CaFZ、AloO3、MgO.、510:等成分在高温下具有适当电导率并具有脱硫、脱磷、去除非金属夹杂熔渣与非金属夹杂物之间的表面张力越小越好，以利物等能力的碱性熔体。熔融渣池是电渣重熔工艺的核于熔渣对非金属夹杂物的浸润、吸附和溶解。心部分，它在金属的熔化、精炼、凝固过程中起着极为其他特性熔渣中不应含有高蒸气压组元，不应重要的作用。含有不稳定氧化物及变价氧化物，以防止熔渣挥发、金 渣的功能电渣重熔渣的功能如下:(1)作为重熔属增氧及元素烧损。同时，渣在固态时应具有一定的抗热源。它把电能转化为电阻热，金属电极依靠熔渣的电湿性，不易发生水合作用。高温时的熔渣应具有较小的阻热进行熔化，并满足熔炼温度的需要。(2)作为净化透气性，防止周围气氛中的氮、氢、氧进入金属熔池;当剂。重熔过程中熔化的金属形成金属熔滴穿过渣池时，铸锭与结晶器相对移动时，为保证渣皮不破裂，获得良渣与金属液滴接触面积很大，利用渣的化学特性可以好的铸锭表面，要求渣皮在高温时具有一定的强度和有效地去除钢中有害元素硫、磷等，去除有害气体氢、塑性等。此外，选择渣系要注意安全性和经济性，熔渣氧、氮等，吸收、溶解熔融金属与渣界面的非金属夹杂应不析出或尽量少析出危害操作人员健康、污染环境物，使金属得到提纯、净化。(3)作为保护剂。它在铸锭的有害气体和灰尘，并尽量因地制宜、选用价格低廉的和结晶器间形成一层渣皮，这层渣皮起到了绝缘、隔原料。热、润滑作用，使金属不与结晶器直接接触，防止了电渣的组元常用渣系的基本形态是以caF:为基分流，使热流主要向底水箱方向传导，结晶趋向纵轴方础，配入适当的cao、A1203、Mgo、5102、TioZ等氧化向，并有利子铸锭和结晶器壁的相对运动。另外，在金物组成的，各组元成分在渣中有各自的作用。(1)caFZ:属熔池上方的熔融渣池使金属液避免直接与大气接能降低渣的熔点、私度和表面张力。但和其他组元相触，起到了防止金属氧化及贮热保温作用。在电渣重熔比，CaFZ的电导率较高，纯caFZ在1650℃时电导率达过程中，金属始终在渣的包覆下熔化、凝固。4·54。一‘·Cm一‘;渣中CaFZ含量高，熔炼中易放出有 渣的选择电渣重熔渣系、配比和渣量的选择对害气体和烟尘，造成环境污染。(2)cao:渣中加入cao电渣钢的冶金质量、熔炼技术经济指标以及环境保护将增大渣的碱度，提高脱硫效率，在cao加入量为具有重大的影响。为了满足各项技术经济指标的要求，40%情况下，脱硫率最高可达到85%;而且cao的加必须从熔点、电导、私度、碱度、表面张力、比热、蒸汽入能够降低渣的电导率。但是CaO吸水性强，易带入压、透气度等各项物理化学性质进行综合考虑，才能选氢和氧，造成钢增氢增氧。(3)A12O。:能明显降低渣的出合理的渣型。电导率，减少电耗，提高生产率。例如caF:90%+ 熔点渣的熔点应低于重熔金属熔点，熔渣成分A12O。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条