1) tetraethyl orthosilicate
正硅酸乙脂
1.
The effects of catalysts and temperature on gelling time in the sol-gel process of TEOS(tetraethyl orthosilicate) are studied,and the surface morphology of the silica films prepared on various substrates observed in the article.
采用溶胶-凝胶法,研究了催化剂和反应温度对正硅酸乙脂溶胶-凝胶过程中胶凝时间的影响,观察了不同基材上制得的SiO2薄膜的表面形貌。
2.
Catalyzed by NaF and NH3·H2O, silica films were prepared with the tetraethyl orthosilicate (TEOS) sol-gel.
采用溶胶-凝胶法,以正硅酸乙脂为原料,NaF、氨水溶液作为催化剂制备SiO2薄膜,研究了催化剂的种类、浓度、加入量及反应温度对正硅酸乙脂胶凝化过程中水解、聚合及胶凝时间的影响,观察比较了SiO2薄膜的表面形貌。
2) TEOS
正硅酸乙酯
1.
The Dynamic Laser Scattering(DLS) Investigation on the Hydrolytic Polycondensation of Tetraethylorthosilicate(TEOS);
正硅酸乙酯水解-缩合过程的动态激光光散射研究
2.
Influences of the Catalyzing Mode and the Ratio of Water on TEOS Sol-Gel Processing;
催化方式和水硅比对正硅酸乙酯的溶胶凝胶过程的影响
3.
The Effect of Catalysts on TEOS Hydrolysis-Condensation Mechanism;
催化剂对正硅酸乙酯水解-聚合机理的影响
3) Tetraethylorthosilicate
正硅酸乙酯
1.
Synthesis of silica film using tetraethylorthosilicate;
利用正硅酸乙酯制备二氧化硅膜
2.
Tetraethylorthosilicate(TEOS) was used as source material and hydrochloric acid or ammonia was used as catalyst to prepare SiO_2.
以正硅酸乙酯(TEOS)为主要原料,乙醇为溶剂,盐酸或氨水等为催化剂可制得硅酸凝胶。
3.
The studies indicate that the order of the grade influencing the average diameter is the water content is in the first place,ethanol the second,ammonia the third,and tetraethylorthosilicate the l.
研究表明:对单分散球形SiO2的平均粒径的影响次序为:用水量、醇用量、氨水和正硅酸乙酯(TEOS)用量。
4) tetraethyl orthosilicate
正硅酸乙酯
1.
Nanosize SiO_(2) particles were prepared using water-in-oil microemulsion method in polyether polyol with hydrolysis and condensation reactions of tetraethyl orthosilicate(TEOS) by means of controlling molar ratio of water to surfactant and selecting moderate hydrolysis temperature.
选择适当的乳化剂和水解温度以及控制水与乳化剂的摩尔比,采用W/O型微乳液法在聚醚多元醇中通过正硅酸乙酯的水解、缩合反应合成了纳米SiO2。
2.
Porous carbons were prepared by using a sol-gel method with tetraethyl orthosilicate (TEOS) as the silica template and sucrose as carbon precursor and adding N,N- dimethyl formamide(DMF) as drying control chemical additive(DCCA).
以正硅酸乙酯(TEOS)为模板硅源,蔗糖为碳前体,添加N,N-二甲基甲酰胺(DMF)作为控制干燥化学助剂(DCCA),运用溶胶凝胶(Sol-Gel)法制备多孔炭材料。
3.
The silica MSU-X type mesoporous molecular sieves were synthesized by using the polyoxyethylene stearyl ether (C18EO10) as template, the tetraethyl orthosilicate (TEOS) and sodium silicates as silica source, respectively.
以十八烷基聚氧乙烯醚(C18EO10)为模板剂,以正硅酸乙酯(TEOS)和硅酸钠分别为硅源,研究了不同pH值、反应温度、反应时间、原料比等条件下,合成的全硅MSU-X型介孔分子筛产物的结构变化规律,并通过焙烧和水热处理,考察了MSU-X介孔材料的结构稳定性。
5) tetraethoxysilane
正硅酸乙酯
1.
Effect of tetraethoxysilanes (TEOS) on the nanomechanical properties of organic-inorganic hybrid films;
正硅酸乙酯对杂化膜纳米力学性能的影响
2.
Influence of tetraethoxysilanes (TEOS) on the interfacial bond strength between organic-inorganic hybrid film and substrate;
正硅酸乙酯对有机无机杂化膜结合强度的影响
3.
Poly(vinyl alcohol)(PVA) was mixed with poly(ethylene glycol)(PEG) and then cross-linked by tetraethoxysilane (TEOS) to prepare organic-inorganic hybrid membranes.
以聚乙烯醇(PVA)与聚乙二醇(PEG)共混,并与正硅酸乙酯(TEOS)进行交联反应制备杂化膜。
6) Elastified silicic acid ester
弹性硅酸乙脂
补充资料：双(仲丁醇)正硅酸三乙基正硅酸酯铝盐
CAS：68959-06-8
分子式：C14H33AlO6Si
分子质量：352.47
中文名称：双(仲丁醇)正硅酸三乙基正硅酸酯铝盐
英文名称：bis(2-butanolato)(triethyl orthosilicato-O''')-Aluminum
di-sec-Butoxyaluminoxytriethoxysilane
bis(2-butanolato)(triethyl orthosilicato-o''')-aluminum
diethoxysiloxane-s-butylaluminate copolymer
分子式：C14H33AlO6Si
分子质量：352.47
中文名称：双(仲丁醇)正硅酸三乙基正硅酸酯铝盐
英文名称：bis(2-butanolato)(triethyl orthosilicato-O''')-Aluminum
di-sec-Butoxyaluminoxytriethoxysilane
bis(2-butanolato)(triethyl orthosilicato-o''')-aluminum
diethoxysiloxane-s-butylaluminate copolymer
说明：补充资料仅用于学习参考，请勿用于其它任何用途。