1) Stabilized zirconia
稳定氧化锆
1.
Crystal phase study of stabilized zirconia collected by dust catcher during airflow pulverization;
稳定氧化锆气流粉碎中除尘料的晶相研究
2) stabilized-zirconia
稳定化二氧化锆
3) YSZ
钇稳定化氧化锆
1.
Study on the Properties of YSZ Electrolyte Fabricatedby Plaster Casting Method;
注浆成型法制备的钇稳定化氧化锆电解质性能研究
2.
The yttria stabilized zirconia (YSZ) porous ceramic tubes with a porosity of 49 0%~64 1% were fabricated by slip casting method with YSZ powder as the aggregate, arabic gum as the dispersant and the binder, and optimized corn meal as the pore forming agent.
以钇稳定化氧化锆 (YSZ)为骨料 ,优选出玉米粉为成孔剂 ,阿拉伯树胶为分散剂和粘结剂 ,采用注浆法制备出孔隙率为 49。
3.
The stability of suspension made of 8% yttria stabilized zirconia (YSZ) micro size powder with 4% Al 2O 3 added and arabic gum as the dispersant was studied.
研究摩尔分数为 8%的钇稳定化氧化锆 ( YSZ)微粉添加质量分数为 4%的 Al2 O3 ,并以阿拉伯树胶为分散剂所制备的料浆的稳定性 。
4) partially stabilized zirconia
部分稳定氧化锆
1.
A partially stabilized zirconia (PSZ) ceramic was prepared by aqueous gelcasting.
用流变学的方法研究了不同条件,如:固相含量、分散剂加入量、烧结助剂、增塑剂等对碱性部分稳定氧化锆(partially stabilized zirconia,PSZ)悬浮体的流变性的影响。
5) Yttrium stabilized zirconia(YSZ)
钇稳定氧化锆(YSZ)
补充资料：稳定化氧化锆制品
分子式：
CAS号：
性质：以二氧化锆为主加入稳定剂组成的制品。氧化锆在多晶转化时发生体积变化，导致产品开裂。加入氧化钙、氧化镁、氧化钇、氧化铈等稳定剂，可形成从室温到2000℃以上都稳定的立方型晶体结构的二氧化锆固溶体。这种制品化学稳定性好，与钢液不浸蚀，高温结构强度大，热导率小[2.2W/(m·K)]、热膨胀系数高(25～1500℃时为9.4×10-6/℃)。一般用二氧化锆作原料，和稳定剂一起细磨，在1450℃下煅烧制取。用于盛钢桶内衬，制造高温发热元件、铂铑等贵金属的坩埚。
CAS号：
性质：以二氧化锆为主加入稳定剂组成的制品。氧化锆在多晶转化时发生体积变化，导致产品开裂。加入氧化钙、氧化镁、氧化钇、氧化铈等稳定剂，可形成从室温到2000℃以上都稳定的立方型晶体结构的二氧化锆固溶体。这种制品化学稳定性好，与钢液不浸蚀，高温结构强度大，热导率小[2.2W/(m·K)]、热膨胀系数高(25～1500℃时为9.4×10-6/℃)。一般用二氧化锆作原料，和稳定剂一起细磨，在1450℃下煅烧制取。用于盛钢桶内衬，制造高温发热元件、铂铑等贵金属的坩埚。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。