The effects of diffusion annealing temperatures and times on the microstructure,component and bond strength of titanium/steel interface were examined by the scanning electron microscope (SEM) observation,energy dispersive spectroscopy (EDX) and electron probe microanalysis (EPMA) measurements and tensi.
将钛管、钢管利用冷拔-内压扩散法制备了内包覆钛-钢复管。
2) titanium steel
钛钢
3) Low Ti steel
低钛钢
4) Ti-killed steel
钛镇静钢
1.
The contact angles of pure Fe, Al-killed steel and Ti-killed steel in contact with Al_2O_3 and MgO substrates were measured by the sessile drop technique.
为了解铝和钛的氧化物在钢中的行为及其夹杂物的去除方法,采用静滴法在1873K及不同氧分压条件下,测定了纯铁、铝镇静钢和钛镇静钢在Al2O3和MgO垫片上的接触角,确认了液滴尺寸与接触角的关系及影响界面张力的因素,并提出了界面行为中线能量的重要性。
6) Nb-Ti-bearing steel
铌钛钢
1.
Test results show that addition cerium (Ce) in low sulfur Nb-Ti-bearing steel affects as follows: Ce can increase the transformation point t_(Ar_3) and t_(Ar_1), enlarge the intervals of temperature (t_(Ar_1)-t_(Ar_3)).
在实验室条件下采用50kg真空感应炉冶炼和两段控制轧制工艺,采用THERMECMASTOR Z热模拟机对过冷奥氏体连续冷却转变曲-tAr1)温度区间增大;并使钢的CCT曲线右移,并且使(tAr3线进行了测定,试验结果表明,低硫铌钛钢中稀土铈能提高钢的临界点tAr3和tAr1和上移,降低了钢的淬透性;铈会使贝氏体转变点升高,同时加大了贝氏体转变间隔;当冷却速度较高时,稀土使马氏体由粗条状变为细条状,降低了Ms点,并且增强了马氏体结构的板条化趋势,抑制了片状晶生成。
补充资料：含钛钢
分子式：
CAS号：
性质： 含有一定量钛的钢。钛和碳、氮、氧都有极强的亲和力，钛在钢中主要以碳化物的形态存在，它是良好的脱氧去气剂及固定碳、氮的有效元素。钛可细化钢的组织和晶粒，并能提高晶粒粗化温度至1000℃以上。由于钛和碳之间的亲和力大于铬与碳，故用来消除不锈钢的晶间腐蚀。钛是强铁素体形成元素，强烈提高A1及A3。固溶的钛可提高淬透性，也可强化铁素体。钛在钢中的含量很低，当钛>0.025%时即认为是合金元素。
CAS号：
性质： 含有一定量钛的钢。钛和碳、氮、氧都有极强的亲和力，钛在钢中主要以碳化物的形态存在，它是良好的脱氧去气剂及固定碳、氮的有效元素。钛可细化钢的组织和晶粒，并能提高晶粒粗化温度至1000℃以上。由于钛和碳之间的亲和力大于铬与碳，故用来消除不锈钢的晶间腐蚀。钛是强铁素体形成元素，强烈提高A1及A3。固溶的钛可提高淬透性，也可强化铁素体。钛在钢中的含量很低，当钛>0.025%时即认为是合金元素。