1) Cu-Al-Ni
Cu-Al-Ni
1.
Cu-Al-Ni wires with columnar grain structure fab- ricated by heated mold continuous casting process were con- ducted bending fatigue and tensile fatigue tests to study the behavior of grain boundaries in fatigue process.
用热型连铸法制取具有柱状晶组织的Cu-Al-Ni合金丝,进行弯曲疲劳和拉伸疲劳试验,研究晶界在疲劳过程中的行为。
2.
Properties have been studied to establish the possibility of industrial application of Cu-Al-Ni SMA with columnar grain structure.
本文对具有柱晶组织的Cu-Al-Ni形状记忆合金丝的性能作了系统的研究，以确定Cu-Al-Ni形状记忆合金在工业化生产中实际应用的可能性。
2) Cu-Al-Ni alloy
Cu-Al-Ni合金
1.
Effects of Ti addition on grain growth of Cu-Al-Ni alloy cast by heated mold continuous casting process;
Ti对热型连铸Cu-Al-Ni合金晶粒长大的阻碍作用
3) Cu-Al-Ni-Be
Cu-Al-Ni-Be
1.
A Study on Shape Memory Performance of Single Crystal Cu-Al-Ni-Be Alloy;
单晶Cu-Al-Ni-Be合金的形状记忆特性研究
4) Cu-Al-Ni alloy
铜-铝-镍合金
1.
Shape memory and supper elasticity properties of the Cu-Al-Ni alloys prepared by ohno continuous casting process were tested after different heat treatment,and the mechanisms were analyzed.
用热型连铸技术制备了铜-铝-镍合金,对经不同热处理后的合金进行了形状记忆和超弹性试验,并分析了相关机理。
5) Cu-Al-Ni shape memory alloy(SMA)
Cu-Al-Ni形状记忆合金
6) Cu-Al-(Ni)-Mn shape memory alloy
Cu-Al-（Ni）-Mn形状记忆合金
补充资料：Cu-A1-Ni shape memory alloy
分子式：
CAS号：
性质：一种含A1 14％～14.5％(质量)、Ni 3％～4.5％(质量)、余者为铜的具有形状记忆效应和伪弹性的合金。其Ms点在133～373K之间。该合金的形状记忆应变约4％，它的热循环特性、形变循环特性和疲劳特性等均比TiNi形状记忆合金差。熔炼与Cu-Zn-A1形状记忆合金相同。该合金加工性很差，冷加工完全不可能。它的另一突出问题是随时间增长而记忆严重衰退的现象，为了提高合金的稳定性，可以进行等温淬火或一般淬火后进行时效处理。在Cu-A1-Ni形状记忆合金基础上开发出的Cu12Al5Ni2MnTi％(质量)五元高温形状记忆合金，铝含量降低，并加入Mn、Ti后，使Ms点提高到473K，同时合金的加工性亦得到改善，使Cu-A1-Ni系形状记忆合金成为具有实用价值的材料。
CAS号：
性质：一种含A1 14％～14.5％(质量)、Ni 3％～4.5％(质量)、余者为铜的具有形状记忆效应和伪弹性的合金。其Ms点在133～373K之间。该合金的形状记忆应变约4％，它的热循环特性、形变循环特性和疲劳特性等均比TiNi形状记忆合金差。熔炼与Cu-Zn-A1形状记忆合金相同。该合金加工性很差，冷加工完全不可能。它的另一突出问题是随时间增长而记忆严重衰退的现象，为了提高合金的稳定性，可以进行等温淬火或一般淬火后进行时效处理。在Cu-A1-Ni形状记忆合金基础上开发出的Cu12Al5Ni2MnTi％(质量)五元高温形状记忆合金，铝含量降低，并加入Mn、Ti后，使Ms点提高到473K，同时合金的加工性亦得到改善，使Cu-A1-Ni系形状记忆合金成为具有实用价值的材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。