1) artificial accelerated ageing test
人工加速老化试验
1.
This paper contrastively analyzes the field exposure test and artificial accelerated ageing test data in the South China Sea about the fluorocarbon coatings for the anticorrosion engineering of Main Gymnasium of Olympic Games and other fluorocarbon coatings, giving the, differences among every type of fluorocarbon resin coatings about their aging-resistance.
介绍了奥运主体育场"鸟巢"防腐工程用氟碳涂料与其它类型氟碳树脂涂料在海南的天然曝晒试验数据与人工加速老化试验数据对比分析,并详细阐述了各种类型氟碳树脂涂料在耐老化性方面存在差异的原因。
2.
The photo-oxidation ageing process of polypropylene filaments was studied by artificial accelerated ageing test using different intensities of UV irradiation.
以聚丙烯长丝为对象,采用不同紫外线辐射强度的人工加速老化试验对其光氧老化过程进行研究。
2) artificial weathering test
人工气候加速老化试验
3) accelerated aging test
加速老化试验，人工老化试验
4) artificial accelerated aging test
人工加速老化实验
5) accelerated aging test
加速老化试验
1.
This article studies the impact of the accelerated aging test to UF MDF decorated by different material about physical and mechanical properties.
研究了加速老化试验对经不同装饰后的脲醛胶中纤板物理力学性能的影响。
2.
A accelerated aging test of ethylene propylene rubber M204 and M209 7 in propellant was carried out.
进行了乙丙胶M 2 0 4和M 2 0 9 7在推进剂中的加速老化试验 ,经过对试验数据的处理 ,初步发现时间外延方法适用于预测橡胶材料在特种介质中的老化性能变
3.
In this paper, the accelerated aging tests at several higher temperatures are carried out for a kind of RDX compound explosive charge used in a certain missile warhead.
通过高温加速老化试验和统计分析,研究了某导弹战斗部中炸药装药的贮存寿命分布规律,在此基础上,建立了贮存寿命的可靠性评估模型,并对贮存温度下的平均贮存寿命及贮存寿命置信下限进行了评估。
6) accelerated ageing test
加速老化试验
1.
The oxidation stability of lubricating oils including 30# machinery oil, 4106# and 4109# aircraft lubricating oils was studied out by accelerated ageing test According to the property-aging time relation and Arrhenius formulation, the ageing dynamic equation of variance ratios of viscosity of 30# machinery oil was obtained by linear regression method.
对30#机械油与4106#和4109#航空润滑油进行了加速老化试验;在此基础上,运用阿累尼乌斯方程和性能变化的时温关系式,采用线性回归方法推导出30#机械油粘度变化的老化动力学方程,以粘度增加率20％为使用极限值,预测它在25℃条件下的贮存年限为12 a。
补充资料：加速臭氧老化试验
分子式：
CAS号：
性质：在强化橡胶受臭氧作用而发生龟裂所进行的试验。常用臭氧天候试验仪进行试验。试验时将试样保持在一定臭氧浓度的试灵腔室内，经受一定伸长，弯曲或周期性伸缩和屈挠作用，从而加速臭氧对橡胶的老化速度。
CAS号：
性质：在强化橡胶受臭氧作用而发生龟裂所进行的试验。常用臭氧天候试验仪进行试验。试验时将试样保持在一定臭氧浓度的试灵腔室内，经受一定伸长，弯曲或周期性伸缩和屈挠作用，从而加速臭氧对橡胶的老化速度。