1) inclusion area
夹杂物面积
1.
Influence of shape and size of inclusion on crack initiation was studied,and the relationship of inclusion area and the initiation stress of the first crack in the inclusion under tensile load was discussed.
同时讨论TiN夹杂中第一条裂纹萌生所需的应力与夹杂物面积的关系。
2) inclusion volume fraction f
夹杂物体积分数f
1.
The effects of the inclusion volume fraction f and the average spacing X0 .
在固定显微组织和夹杂物抗空穴形核能力因素的基础上,分析夹杂物体积分数f、夹杂物平均间距X0对临界裂纹尖端张开位移δIc的影响,得出高Co-Ni超高强度钢临界裂纹尖端张开位移与夹杂物体积分数f-1/3和平均间距X0呈线性关系。
3) surface inclusions
表面夹杂
1.
This paper studies the problem of surface inclusions and cracks of continuous casting slab at Maanshan Steel and puts forward corresponding measures to solve the problem.
针对马钢板坯连铸生产过程中出现的表面夹杂与裂纹进行分析研究,提出了改进措施。
4) surface inclusion
表面夹杂
1.
Results indicate that surface inclusions can be reduced and physical product quality of steel improved by taking a few proper measures including the use of high quality mould powder and refactory mate- rial and an increase in amount of final deoxidizing Al.
分析脱氧加铝量、中间包加铝操作、结晶器保护渣及中间包耐火材料等工艺操作因素对16MnR钢板表面夹杂的影响。
2.
Against the characteristics of surface inclusions of medium plate,the resources of inclusions,the influence of the performances and shape of casting powder to inclusions were analyzed.
针对柳钢中板表面夹杂物缺陷的特点,分析了夹杂物的来源和保护渣性能、形态对夹杂物的影响。
6) inclusions
夹杂物
1.
Research on inclusions in billet continuous casting of steel ML08Al;
ML08Al冷镦钢连铸坯中夹杂物的研究
2.
New technology for control and removal of inclusions in tundish;
中间包夹杂物的去除与控制新技术
3.
Formation and Control of Inclusions in Si-Mn Cast Steel with High Carbon Content;
高碳硅锰铸钢中夹杂物的形成与控制
补充资料：GCr15钢中的大型非金属夹杂物(铝酸盐)×500
GCr15钢中的大型非金属夹杂物(铝酸盐)×500
GCrl5钢中的大型非金属夹杂物(铝酸盐) ×500