1) macromolecular surface treatment agent
大分子改性剂
2) macromolecular modifier
大分子表面改性剂
1.
Tricopolymer macromolecular modifier, MAA-BA-AN,was synthesized by radical polymerization from methacrylic acid(MAA),butyl acrylate(BA) and acrylic nitrile(AN).
以甲基丙烯酸(MAA),丙烯酸丁酯(BA)和丙烯腈(AN)为单体,通过自由基溶液聚合法合成了MAA-BA-AN三元共聚物大分子表面改性剂,其结构和性质经1HNMR,13C NMR,FT-IR,GPC,TGA及DSC等表征。
2.
In this work,a new macromolecular modifier butyl acrylate-methyl methacrylate-vinyltriethoxysilane(BA-MMA-VTES tercopolymer)was synthesized via radical polymerization under optimum conditions adopting BPO and DCP as initiators.
针对弱极性天然/丁苯橡胶复合体系,从分子设计的角度出发,选择乙烯基三乙氧基硅氧烷(VTES)、丙烯酸丁酯(BA)、甲基丙烯酸甲酯(MMA)为单体,通过自由基溶液聚合并优化了反应条件:在85℃和115℃分别加入两种不同量的引发剂BPO和DCP,均保温反应2h,合成了三元共聚物BA-MMA-VTES大分子表面改性剂,用于纳米碳化硅、氮化硅陶瓷粉体的表面改性。
3) macromolecular surface modifier
大分子表面改性剂
1.
The inducement of contacting media and rejection of crystallization of polyolefins leading to the aggregation of macromolecular surface modifiers on the surface of polymers were studied.
简述了大分子表面改性剂添加到聚烯烃基体中时接触介质的诱导作用和聚烯烃基体结晶的异质排斥作用及其相对分子质量、链节的柔顺性和与基体的相容性对其表面富集的影响。
2.
The hydrophilicity of polypropylene surface can be obviously improved by blending the polypropylene with a macromolecular surface modifier graft copolymer of methacrylic acid and random polypropylene (APP-g-MAA) and a graft copolymer of methacrylic acid and polypropylene wax (PPw-g-MAA),respectively.
将大分子表面改性剂无规聚丙烯-甲基丙烯酸接枝共聚物(APP_g_MAA)和聚丙烯蜡-甲基丙烯酸接枝共聚物(PPw_g_MAA)与聚丙烯(PP)进行共混,能极大地提高聚丙烯的表面润湿性能。
3.
A self-made macromolecular surface modifier acrylate-methyl methacrylate-vinyl triethoxy silane(BA-MMA-VTES)was used for surface modification of nano-sized Silicon Nitride(Si3N4) ceramic power and the modified nano-Si3N4 powder was added to hydrolysis-resistance polyurethane(PU) leather.
采用自制的丙烯酸丁酯-甲基丙烯酸甲酯-乙烯基三乙氧基硅氧烷(BA-MMA-VTES)大分子表面改性剂对纳米氮化硅(Si3N4)陶瓷粉体进行表面包覆改性,将改性后的纳米Si3N4粉体加入到耐水解聚氨酯(PU)树脂中成革,并进行傅立叶变换红外光谱、透射电子显微镜等分析及力学性能测试。
4) surface modifying macromolecules
大分子表面改性剂
1.
The development and the essential assortment of the surface modifying macromolecules(SMM) were general summarized and the fundamental principles about the design and synthesis of the surface modifying macromolecules were discussed.
简述大分子表面改性剂的发展过程和基本分类,提出大分子表面改性剂设计合成的基本原则,即化学结构和使用环境相匹配、憎水基功能团和亲水基功能团相适应、使用效率和功能持久性相平衡。
5) macromolecule interfacial modifier
大分子界面改性剂
1.
With the measurement of mechanical properties and analysis of SEM, effects of selfmade macromolecule interfacial modifier on the mechanical properties of PA6/brucite composites were studied, and they were compared with those of coupling agent TC-114.
通过力学性能测试及扫描电子显微镜分析 ,探讨了自制的大分子界面改性剂对PA6 /水镁石力学性能的影响 ,并与偶联剂TC - 114进行了对比。
6) polymeric modifier
高分子改性剂
1.
The cold resistance and medium resistance of soft PVC blend with various polymeric modifiers were studied by brittleness temperature test,dynamic mechanical test, Gehman test and Ross flex test.
本文通过脆性温度试验、动态力学试验、吉门试验和Ross屈挠试验,研究了用不同高分子改性剂共混改性的软质聚氯乙烯的耐寒性能和耐介质性能。
补充资料:吸附剂类高分子氧化剂
分子式:
CAS号:
性质: 指以各种吸附剂为载体,利用分子间的吸附作用与小分子氧化剂结合得到的高分子氧化剂。其中所用的吸附剂可以是硅藻土、硅胶、石墨和分子筛等无机吸附剂和人工合成高分子有机吸附剂,采用的小分子吸附剂包括金属氧化物,如Ag2CO3、CrO3,气体型氧化剂,如臭氧等,和小分子液体氧化剂,如三氯乙醛等。上述氧化剂被吸附以后稳定性增加,使用更加方便,而且价格低廉。如硅胶在低温下吸附臭氧,能使烃基羟基化,或者将仲醇氧化成醛,在常规液相反应条件下操作困难。由于吸附剂与氧化剂之间的吸附力与温度关系密切,温度低,吸附性强,因此吸附剂类高分子氧化剂多在低温下反应,利用提高温度脱吸附可以使吸附剂再生回收。
CAS号:
性质: 指以各种吸附剂为载体,利用分子间的吸附作用与小分子氧化剂结合得到的高分子氧化剂。其中所用的吸附剂可以是硅藻土、硅胶、石墨和分子筛等无机吸附剂和人工合成高分子有机吸附剂,采用的小分子吸附剂包括金属氧化物,如Ag2CO3、CrO3,气体型氧化剂,如臭氧等,和小分子液体氧化剂,如三氯乙醛等。上述氧化剂被吸附以后稳定性增加,使用更加方便,而且价格低廉。如硅胶在低温下吸附臭氧,能使烃基羟基化,或者将仲醇氧化成醛,在常规液相反应条件下操作困难。由于吸附剂与氧化剂之间的吸附力与温度关系密切,温度低,吸附性强,因此吸附剂类高分子氧化剂多在低温下反应,利用提高温度脱吸附可以使吸附剂再生回收。