1) stress corrosion cracking
应力腐蚀破裂
1.
Alkali cleaning and stress corrosion cracking in petrochemical equipment;
石化设备碱洗与应力腐蚀破裂
2.
The effect of micro-alloying elements on the behavior of stress corrosion cracking of the weld metal;
微合金元素对焊缝金属应力腐蚀破裂性能的影响
3.
Progress in the research on stress corrosion cracking of dental casting alloys;
齿科铸造合金应力腐蚀破裂的研究进展
2) SCC
应力腐蚀破裂
1.
SCC initiated from outside surface and induced by chloride ions was the main failure reason.
通过对盐酸塔不锈钢壳体的化学成分、金相、断口、介质等分析,寻找产生裂纹的原因,外壁氯离子环境造成的应力腐蚀破裂(SCC)是不锈钢失效的主要原因,对此提出采取对下部壳体外壁喷涂环氧树脂,以隔断腐蚀介质的侵蚀,3年来使用情况良好。
2.
The SCC behavior of 316 stainless steel in high temperature water containing 5ppm Cl~- at 300℃ was studies using slow strain rate tests.
采用慢应变速率试验(SSRT)技术研究了固溶态的和敏化态的316型不锈钢在含5ppm Cl~-的300℃高温水中子不同电位下的应力腐蚀破裂(SCC)行为,并对SCC试样表面膜进行了俄歇电子能谱(AES)分析。
3.
The influence of water stabilizer Rp-04L on stress corrosion cracking (SCC) of 304 stainless steel was investigated in simulated hard cooling water by means of electrochemical tests under constant strain and slow strain rate tests (SSRT).
结果表明:水质稳定剂Rp-04L对304不锈钢在高硬度循环冷却水中的应力腐蚀破裂有明显的抑制作用。
3) stress corrosion cracking(SCC)
应力腐蚀破裂(SCC)
4) HSCC
氢应力腐蚀破裂
5) SCC
应力-腐蚀破裂
6) stress corrosion cracking
应力腐蚀裂缝，应力腐蚀裂纹，应力腐蚀破裂
补充资料：应力腐蚀破裂
分子式：
CAS号：
性质：又称应力腐蚀开裂或应力腐蚀(stress corrosion)。材料在静拉伸应力和腐蚀介质共同作用下发生的脆性破裂。大多数合金材料以及一些工程塑料都会发生这种腐蚀破裂。但对于特定材料，破裂通常发生在特定介质中，例如奥氏体不锈钢在氯离子介质中，高强钢在海水中，黄铜在氨溶液中。应力腐蚀裂纹形成后不断扩展，很难监测或控制，最终可导致材料断裂，是工程实践中危害性最大的一种腐蚀类型。可以通过控制介质的化学组成、减小外加应力或在材料表层形成压应力、涂刷表面保护层、缓蚀剂及阴极保护等方法予以防止或减缓。
CAS号：
性质：又称应力腐蚀开裂或应力腐蚀(stress corrosion)。材料在静拉伸应力和腐蚀介质共同作用下发生的脆性破裂。大多数合金材料以及一些工程塑料都会发生这种腐蚀破裂。但对于特定材料，破裂通常发生在特定介质中，例如奥氏体不锈钢在氯离子介质中，高强钢在海水中，黄铜在氨溶液中。应力腐蚀裂纹形成后不断扩展，很难监测或控制，最终可导致材料断裂，是工程实践中危害性最大的一种腐蚀类型。可以通过控制介质的化学组成、减小外加应力或在材料表层形成压应力、涂刷表面保护层、缓蚀剂及阴极保护等方法予以防止或减缓。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。