1) PTFE composite membrane material
聚四氟乙烯复合膜材料
2) PTFE composites
聚四氟乙烯复合材料
1.
Experimental results showed that the best tribological behavior of the CF/PTFE composites was obtained when the content of rare earth elements was 0.
3%时,炭纤维填充聚四氟乙烯复合材料的摩擦磨损性能最佳;在干摩擦条件下,表面处理炭纤维填充聚四氟乙烯复合材料的摩擦系数比未经处理炭纤维填充聚四氟乙烯复合材料的低,且其耐磨性较好;稀土处理使得复合材料的界面强韧性得到明显改善,从而提高了其摩擦磨损性能。
2.
Experimental results revealed that the friction properties of PTFE composites filled with surface treated carbon fibers were better than those of the composite filled with untreated carbon fibers,while RE surface treated carbon fiber reinforced.
结果表明：在干摩擦条件下,表面处理碳纤维填充聚四氟乙烯(CF/PTFE)复合材料的摩擦系数比未经处理碳纤维填充聚四氟乙烯复合材料的低,而稀土处理碳纤维填充聚四氟乙烯复合材料具有最低的摩擦系数。
3.
The friction and wear properties of graphite/PTFE composites filled with different content nano-SiC have been studied in this article.
考察了不同含量的纳米SiC对石墨/聚四氟乙烯复合材料摩擦磨损性能的影响,采用扫描电子显微镜分析了磨损表面,并探讨了其磨损机理。
5) polytetrafluoroethylene matrix composite
聚四氟乙烯树脂复合材料
补充资料：聚四氟乙烯复合材料
聚四氟乙烯复合材料
polytetrafluoroethylene matrix composites
聚四报乙烯复合材料polytetrafluor。ethylenematrix comPo滋tes以聚四氟乙烯树脂为基体、用纤维增强或坡料填充制得的复合材料。聚四氛乙姗是四氟乙烯单体的加聚产物，属结晶性热塑性塑料。其熔点327OC，能在一250一+260℃范围内长期使用，有出色的化学稳定性、突出的表面不枯性、优异的介电性和自润滑性，摩擦系数很低。但抗蠕变性和机械强度较差，熔体粘度很高，难以用一般热塑性塑料的成型方法成型。聚四佩乙烯复合材料中常用的增强纤维几是玻璃纤维、碳纤维与石格纤维，常用的填料有青铜粉、石墨和二硫化相等。纤维增强复合材料常用分散法制造的聚四氟乙烯树脂浓缩水分散乳液浸演、喷涂或涂刷纤维，然后冷压烧结制成。烧结温度约375℃。与未增强纯聚四氟乙烯相比，含10一25%(体积分数)超短玻璃纤维的增强聚四氟乙烯的耐磨性高1000倍;用高模量碳纤维填充的聚四氟乙烯在200℃下的抗蠕变性大幅度提高，在水中的抗磨损能力比玻璃纤维增强聚四氟乙烯还要好;填充50~70%(重量分数)青铜粉或青铜粉与石墨(或二硫化钥)并用的填充聚四氟乙烯的摩擦性大大改善。聚四报乙烯复合材料主要用于制作无油润滑耐磨轴承、活塞环、密封环;耐蚀化工管道、装置、衬里;高频绝缘材料，通信电缆、耐磨包筱电线等。还可制造高性能导弹雷达罩。(过梅丽)‘