1) Multi-layer Spray Deposition
多层喷射沉积
1.
Mechanism of multi-layer spray deposition of bimetal;
多层喷射沉积制备双金属板材的机理初探
2.
By the application of programmable controller in the preparation technology of multi-layer spray deposition,automatic control over scanning movement of the spray system and withdrawal movement of the preform can be executed to regulate the outline and size of deposited blanks more precisely.
在多层喷射沉积管坯与柱坯制备工艺中 ,采用可编程调节器可实现喷射系统扫描运动与坯体下降运动的自动控制 ,较精确地控制沉积坯的外形、尺寸 ,制备出了尺寸达Φ外650 /Φ内 3 60mm ,长 12 0 0mm的各种铝合金管坯与Φ30 0～ 50 0mm的铝合金柱
3.
7Si alloy tubes are prepared by multi-layer spray deposition.
采用多层喷射沉积装置与技术制备 外 6 5 0 / 内 3 6 0× 12 0 0mm的大型厚壁Al- 8。
2) multi layer spray deposition
多层喷射沉积
1.
It shows that multi layer spray deposition have many merits, for example: simple techniques, high adhesion strength etc.
采用多层喷射沉积技术制备铝 /钢双金属板 ,分析了其中对双金属板界面结合产生影响的因素。
2.
Large scale 6066Al/SiC p/Gr composite tube with size up to 650mm in outer diameter, 300 mm in inner diameter and 800 mm in length has been prepared by multi layer spray deposition and twin atomizer system, and then extruded into tube product of 350 mm in outer diameter and 250 mm in inner diameter.
采用多层喷射沉积技术与双喷嘴雾化系统制备了外径为 6 5 0mm ,内径为 30 0mm ,长为 80 0mm的大尺寸6 0 6 6Al/SiCp/Gr颗粒增强复合材料管坯 ,并成功挤压外径为 35 0mm ,内径为 2 5 0mm的管材 。
3.
A hypereutectic Al Si Cu Mg alloy is fabricated by multi layer spray deposition technology which has more advantages than the traditional spray deposition such as higher cooling rate, simple technological route and lower oxidation.
多层喷射沉积技术具有冷速快、工艺简单、氧化程度低、制备的材料组织细小且分布均匀等特点 。
3) multi-layer spray co-deposition
多层喷射共沉积
4) spray deposition
喷射沉积
1.
Application of spray deposition technology in aluminum-silicon electronic;
喷射沉积技术在Al-Si电子封装材料中的应用
2.
Numerical simulation for preparing φ520/φ460 mm pipe of spray deposition heat-resistant alunimun alloy;
非致密喷射沉积耐热铝合金锭坯制备φ520/φ460mm管材过程数值模拟
3.
Microstructure and corrosion resistance of spray deposition ZA35 Alloy;
喷射沉积ZA35合金组织与耐蚀性
5) spray-deposition
喷射沉积
1.
5Cu-1Mg-1V alloy was prepared by spray-deposition technology,a kind of rapid solidification.
采用喷射沉积快速凝固技术制备了Al-17Si-5Fe-2Mn-2Ni-3。
2.
5Cu-1Mg-1V alloy was prepared by spray-deposition technology.
针对快速凝固技术可以有效地改变高硅铝合金中初晶硅的形态和尺寸,显著改善合金的使用性能的特点,采用喷射沉积快速凝固技术制备了Al-17Si-5Fe-2Mn-2Ni-3。
3.
As an advanced materials preparation technology,spray-deposition has shown remarkable superiority in producing large-sized alloys and metal matrix composites.
坩埚移动式喷射沉积技术作为一种先进的材料制备新技术,在制备大尺寸合金及金属基复合材料方面具有显著的优越性。
6) Spraying Deposition
喷射沉积
1.
Microstructure of Spraying Deposition Forming Zn-Al Alloy;
喷射沉积锌铝合金原始沉积坯组织形貌研究
2.
The rough blank of Si-Al alloy is prepared by self-made spraying deposition apparatus, the texture of rough blank and the structure evolution after solid solution treatment are analyzed, and the properties for stretching, abrasion and surface-hardness are determined.
用自行研制的喷射装置制备硅铝合金坯体 ,分析喷射沉积坯体的组织结构及固溶处理后的组织变化 ,测试对热挤压后坯件拉伸、表面硬度、耐磨等性能。
3.
Silver thick film conductor was fabricated directly on ceramic substrate by micro-atomization(Microjet) spraying deposition.
采用微细雾化喷射沉积直写的方法在陶瓷基板上制备银厚膜导体。
补充资料：多层沉积层
分子式：
CAS号：
性质：由两种或两种以上相继沉积的金属构成的沉积层。这些沉积层可以由不同特性的同一金属或不同金属构成。如为了提高镍镀层的防护性，有时采用双层镍或三层镍镀层。又如为防护-装饰目的采用的铜/镍/铬三层镀层。
CAS号：
性质：由两种或两种以上相继沉积的金属构成的沉积层。这些沉积层可以由不同特性的同一金属或不同金属构成。如为了提高镍镀层的防护性，有时采用双层镍或三层镍镀层。又如为防护-装饰目的采用的铜/镍/铬三层镀层。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。