1) low carbon manganese steel
低碳锰钢
1.
Influences of deformation parameters on microstructures and mechanical properties of low carbon manganese steel
变形制度对低碳锰钢组织性能的影响
2.
Controlled rolling and controlled cooling experiments under various technology parameters have been carried out on low carbon manganese steels.
在实验室对低碳锰钢进行了控轧控冷试验。
3.
Thermo-mechanical controlled process (TMCP) experiments with finish-rolling temperatures (FRT) higher than Ar3 and different coiling temperatures (CT) have been carried out on a low carbon manganese steel.
对一种低碳锰钢进行了终轧温度高于Ar3卷取温度的不同控轧控冷处理。
2) carbon manganese steel
低锰碳钢
3) low carbon steel strips
低碳含锰钢
1.
Superficial banded structure and its effects on bending flaws of low carbon steel strips;
分析在热轧低碳含锰钢板上观察到的表面带状组织,讨论了带状组织形成的原因和预防方法。
4) low carbon Mn Nb steel
低碳锰铌钢
1.
The temperature time diagram for low carbon Mn Nb steel at constant magnetic field was measured by X—Y recorder, and the beginning temperature of γ→α phase transformation was determined.
用 X— Y记录仪测定了低碳锰铌钢在稳恒磁场下的温降曲线 ,分析标定了奥氏体向铁素体转变的起始相变点 ,通过对空冷至不同温度后淬火试样金相显微组织的分析 ,研究了稳恒磁场对 γ→ α相变的影响。
5) Low carbon silicon manganese
低碳锰硅钢
6) low-cabon-high-msnganese steel
低碳高锰钢
补充资料：超低碳不锈钢
分子式：
CAS号：
性质：含碳量低于0.03％的不锈钢，一般指奥氏体不锈钢。不锈钢中的碳含量降低到0.03％以下，即超低碳化，能有效地避免不锈钢出现贫铬区和防止晶间腐蚀敏感性。碳在铁素体不锈钢中的危害更加严重，当大约从927℃；以上快冷时就会沿晶界析出铬的碳化物，形成晶界贫铬区，而在腐蚀环境中容易发生晶间腐蚀，为了避免晶间腐蚀就要求碳含量必须低于0.01％。采用氩氧脱碳精炼法和真空氧脱碳精炼法，都能生产超低碳不锈钢。
CAS号：
性质：含碳量低于0.03％的不锈钢，一般指奥氏体不锈钢。不锈钢中的碳含量降低到0.03％以下，即超低碳化，能有效地避免不锈钢出现贫铬区和防止晶间腐蚀敏感性。碳在铁素体不锈钢中的危害更加严重，当大约从927℃；以上快冷时就会沿晶界析出铬的碳化物，形成晶界贫铬区，而在腐蚀环境中容易发生晶间腐蚀，为了避免晶间腐蚀就要求碳含量必须低于0.01％。采用氩氧脱碳精炼法和真空氧脱碳精炼法，都能生产超低碳不锈钢。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。