1) welding speed
焊接速度
1.
Relation of welding speed and heat input at aluminum alloy friction stir welding
铝合金搅拌摩擦焊时焊接速度与热输入的关系
2.
The impact of different welding speeds on the low-cycle corrosion fatigue life of 12Cr18Ni10Ti steel sheets in corrosive media was studied and the results showed that,at the same welding process parameters,the low-cycle corrosion fatigue life of steel sheets welded at the speeds ranging from 60 m/hr.
文章研究了不同的焊接速度对12Cr18Ni10Ti薄板在腐蚀性介质中的低用腐蚀疲劳寿命的影响。
3.
The effect of processing parameters including laser power,welding speed and protection gas flow on the welding quality was researched in this paper.
探讨了焊接工艺参数包括激光功率、焊接速度、正反面保护气体流量对焊接效果的影响。
2) bonding speed
焊接速度，接合速度
3) maximum welding speed
最大焊接速度
1.
A detailed CO2 laser-MIG (metal inert gas) hybrid welding experiment was carried out on the 4mm mild plates to discuss the relation of laser power, arc current, the maximum welding speed and the weld shaping, as well as the joint gap.
对此,采用4mm厚Q235钢板进行了CO2激光-MIG(metalinertgas)复合焊接研究,探讨了激光功率、电弧电流对最大焊接速度的影响及其和接头间隙对焊缝成形的影响规律。
4) Speed and power of soldering
焊接速度与功率
5) high-speed welding
高速焊接
1.
Improvement on high-speed welding technology of robot;
弧焊机器人高速焊接工艺改进
2.
The hardware/software configurations, organization and property of high-speed welding system and the technology of high-speed welding for profiled rolle steel was introduced in this paper.
介绍了多源钨极氩弧焊异型钢材高速焊接系统软 /硬件设计、构成、性能和高速焊接工艺 ,此系统在型材轧制生产线上得到了应
6) high speed welding
高速焊接
1.
The theory of stability of a liquid with free surface is applied to understand the ‘humping’ phenomenon in bead formation during high speed welding.
应用具有自由表面的流体稳定性理论，解释了高速焊接时驼峰焊道的产生机理，并通过对熔池形成过程的实时图像采集对该理论进行了验证。
2.
If the generation mechanism of weld bead defects is understood and some suppression measures are proposed, then some improvements can be made for conventional arc welding process so that low-cost and widely used high speed welding process is obtained.
如果针对常用的电弧焊,研究焊接速度提高时焊缝成形缺陷的形成机理,进而提出一定的抑制措施,在此基础上对常规电弧焊工艺做适当改进,得到一种成本低廉、可广泛推广的高速焊接工艺,对于大幅度提高焊接生产效率具有重要的理论意义和工程实用价值。
3.
And it is proved that hard arc is more stable under lower voltage,which is suitable for high speed welding.
在数字控制绝缘栅极晶体管逆变电源平台基础上,研究了短路过渡高速焊接工艺的参数匹配和波形控制规律。
补充资料：Solid Edge焊接设计
Solid Edge在装配环境中还提供一套专用命令用于焊接件的设计。焊接是在装配环境中在指定焊接件上设计焊缝、表面处理、焊接标注和焊后加工处理等。Solid Edge的制图模块可产生焊前和焊后视图，从而完整表达焊接工序。
专业焊接设计工具
装配环境中的装配特征功能，能提供各种的材料处理的能力，如：材料去除、倒角、旋转拉伸、放样拉伸、打孔等，满足焊前表面预处理、添加焊料到焊后机加工等。用户可以采用和零件设计中一样的设计方法，去完成各种各样的操作，而无需学习新的操作命令。与加工过程一致的控制界面既便于学习，又提高了设计效率。
焊前预处理
使用装配特征提供的诸如倒角、开孔、除料等命令对施行焊接的构件表面进行材料去除的操作，该类操作行业上称之为焊前处理，如采用各种手段打坡口等。
添加焊筋
在焊接处可以添加焊料以反映焊接后机件的真实状况。也可以对焊缝进行标注，以便在生成工程图时直接引用。Solid Edge可以提供自动角焊、坡口焊、跳焊等方法，同时也可以利用Solis Edge提供的多种材料添加功能，用手工的方法定义各种类型的特殊形状的焊筋。
焊后机加工
焊接件完成以后，可以对焊接件进行开孔等机加工。此时添加的特征不会对原来的零件产生影响。