1) magnetic aging
磁时效
1.
Combining with the quality control level of high-quality magnetic iron of Taigang and the test methods of magnetic aging,improving process of artificial aging was put forward.
阐述了电磁纯铁的磁时效现象及其机理,并结合太钢无磁时效优质电磁纯铁的质量控制水平和磁时效检验方法,提出了人工时效处理的改进工艺。
2) equivalent instantaneous reluctance
等效瞬时磁阻
1.
With sufficient consideration to realistic application factor of UHV transformer end connecting with long-distance transmission line, and with corresponding calculation for transformer equivalent instantaneous reluctance using adaptive digital low-pass filter, this scheme is good for solving problem.
针对特高压大容量三相分体变压器差动保护,提出一种基于磁特性的励磁涌流快速识别新方案,该方案充分考虑了特高压变压器端部接长距离输电线路的实际特点,配合自适应数字低通滤波器计算变压器等效瞬时磁阻,有效解决了内部故障时由于变压器模型简化造成的计算误差问题。
3) reversible magnetic aging
可逆性磁时效
4) time effect of magnetic hysteresis
磁滞性时间效应
5) aging of permanent magnets
永磁材料的时效
6) equivalent instant excitation inductance
等效瞬时励磁电感
1.
According to the mechanism of producing transformer excitation surge current caused by saturation of transformer core, the paper put forward a kind of method to discriminate excitation surge current and short-circuit current adopting calculation of equivalent instant excitation inductance average value.
从变压器励磁涌流的产生是由于变压器铁心饱和这一原理出发,提出了一种利用计算等效瞬时励磁电感平均值来区分励磁涌流与短路电流的方法。
补充资料：磁时效
磁性材料的磁性随使用时间而变化的现象称为磁时效。这种现象主要是碳和氮等杂质元素引起的。如电工钢板由高温冷却时，多余的碳和氮来不及析出，形成过饱和固溶体。这种钢板制成的铁芯,在长期运转期间,特别在温度升高（20～80℃）时，碳和氮等以细小Fe3C和Fe16N2质点析出，以致使矫顽力和铁损增高。
为检查材料的磁时效情况，通常经100℃×600小时，120℃×120小时或150℃×100小时人工时效,再测量时效前后的矫顽力或铁损的增长率。一般要求矫顽力或铁损增长率小于6％。
为检查材料的磁时效情况，通常经100℃×600小时，120℃×120小时或150℃×100小时人工时效,再测量时效前后的矫顽力或铁损的增长率。一般要求矫顽力或铁损增长率小于6％。