1)  H2Fe2Ti3O10
H2Fe2Ti3O10
1.
A new nanocomposite,H2Fe2Ti3O10/TiO2 was synthesized by the stepwise intercalation reactions of H2Fe2Ti3O10with n-C3H7NH2/C2H5OH mixed solution and acid TiO2 colloid solution.
在高压汞灯辐照下,通过插入反应将H2Fe2Ti3O10与n-C3H7NH2/C2H5OH和TiO2溶胶制备出H2Fe2Ti3O10/TiO2插层复合物。
2)  K2Pr2Ti3O10
K2Pr2Ti3O10
1.
Series of layered perovskites K2Pr2Ti3O10 was fabricated by solid state reaction in K2CO3-Pr2O3-TiO2 system.
在K2CO3-镧系元素氧化物(Pr2O3)-TiO2三元体系中,用固相反应法合成K2Pr2Ti3O10,利用X射线粉晶衍射仪对K2Pr2Ti3O10进行扫描测定,获得X射线衍射数据,进行指标化,得到其晶胞参数。
2.
Layered K2Pr2Ti3O10 is prepared by stearic acid method at lower temperature,and its acid-exchanging process is investigated.
采用硬脂酸法在相对较低的温度下制备了K2Pr2Ti3O10层状化合物,并研究了该化合物的酸交换过程。
3)  K2La2Ti3O10
K2La2Ti3O10
1.
In this paper,the layered perovskite type oxide K2La2Ti3O10 was prepared by high temperature solid state reaction,and was characterized by XRD,UV-vis DRS,and TEM.
用高温固相法合成了具有类钙钛矿型结构的层状化合物K2La2Ti3O10,用XRD、TEM、UV-DRS对其进行表征。
补充资料：Fe-C-O和Fe-H-O系平衡图
    　　铁及其氧化物与CO-CO2或 H2-H2O 混合气体达到平衡时的气相组成与温度的关系图（图1）。它是由实验测得的数据绘制的，是冶金过程物理化学常用的一种优势区图。图中三条线分别代表下列三个反应的平衡气相组成：
　　
570℃以下：Fe3O4+4CO3Fe+4CO2 (1)


　　
570℃以上：Fe3O4+CO3FeO+CO2 (2)


　　
FeO+COFe+CO2 (3)


　　3Fe2O3+CO─→2Fe3O4+CO2反应达平衡时的一氧化碳分压值太小,几乎与横坐标重合,图中未标出。如果实际气相组成pco/(pco+pco2)高于平衡组成,则反应将向右进行,此时反应式等号右边的固相是稳定的,左边的固相不稳定。图中每条线上方的区域就是该反应式右边固体的稳定存在区。这三条线将整个图划分为三个区域，即Fe、FeO、Fe3O4的稳定存在区。三条线交点是四相（Fe、FeO、Fe3O4及气相）共存点（见相图）。
　　
　　
　　在钢铁冶炼过程中，常利用此图来确定在给定温度和气相组成条件下能够稳定存在的固相。此图还明确表明铁的各级氧化物是逐级转化的（见Fe-O 状态图）。
　　
　　由图1可见,在虚线(Fe-H-O平衡)与实线(Fe-C-O平衡)交点温度(820℃)以上,H2比CO具有更强的还原能力；在820℃以下,则正相反。
　　
　　CO对铁还有渗碳作用。当气体中的比值pco/(pco+pCO2)超过反应(4)的平衡组成时，会发生铁的渗碳反应：
　　
2CO(气)─→CO2(气)+[C] (4)

[C]表示溶解于铁中的碳。图2绘出了一系列 [C]含量下渗碳反应达到平衡时的气相组成与温度的关系曲线。此图直接示出在给定温度和[C]含量的情况下,气相对铁是渗碳还是脱碳。这类问题在钢的热处理时经常遇到。FeO是非化学计量化合物(见Fe-O 状态图)，其中氧含量与其平衡气相组成的关系也在图2中绘出。
　　

说明：补充资料仅用于学习参考，请勿用于其它任何用途。