1) alloy carbonizing steel parts
合金渗碳钢件
2) Alloy carburizing steel
合金渗碳钢
1.
The microstructure and property of alloy carburizing steel forged parts after general normalizing and isothermal normalizing were studied.
研究了合金渗碳钢锻件的普通正火与等温正火工艺参数对组织、性能的影响。
4) high alloy carburation steel
高合金渗碳钢
5) Cr-Mn alloy carburizing steel
Cr-Mn合金渗碳钢
6) Alloy cementite
合金渗碳体
1.
Special heat treatment was used to precipitate numerous and fine alloy cementites directly in low temperature tempering,and then realize ultra-hardness via high-carbon matensitic hardening and precipitation strengthening of fine dispersed alloy cementites,the size of the cementites is refined to about 50 nm and the hardness of the cutting tool steel reaches HRC 68-72.
深入分析了有机物切割刀具用钢9CrV通过低温二次硬化实现超硬化的技术原理,采用特殊热处理工艺,在低温回火时直接析出大量微细的合金渗碳体,通过高碳马氏体强化叠加微细弥散合金渗碳体的沉淀强化可显著提高钢的硬度实现超硬化,合金渗碳体的尺寸细化到50 nm左右,由此使钢的热处理硬度达到HRC 68~72。
补充资料：渗碳钢
分子式：
CAS号：
性质：可经受渗碳淬火使表面硬度和耐磨性提高而心部保持适当强度和韧性的钢。其成分特点是低的含碳量，一般为0.1%～0.25%；主要合金元素有Ni、Cr、Mn等，辅助合金元素有W、Mo、V、Ti等。其热处理的特点是，对于低强度的15Cr和20Cr多则，渗碳后应直接淬火或二次淬火；中强度的20CrMnTi钢渗碳后应直接淬火；高强度的18Cr2Ni4W4钢渗碳后应采取空冷、高温回火，这样能使零件满足其在机械性能上的要求。渗碳钢主要用于制造齿轮、凸轮、活塞销等零件。
CAS号：
性质：可经受渗碳淬火使表面硬度和耐磨性提高而心部保持适当强度和韧性的钢。其成分特点是低的含碳量，一般为0.1%～0.25%；主要合金元素有Ni、Cr、Mn等，辅助合金元素有W、Mo、V、Ti等。其热处理的特点是，对于低强度的15Cr和20Cr多则，渗碳后应直接淬火或二次淬火；中强度的20CrMnTi钢渗碳后应直接淬火；高强度的18Cr2Ni4W4钢渗碳后应采取空冷、高温回火，这样能使零件满足其在机械性能上的要求。渗碳钢主要用于制造齿轮、凸轮、活塞销等零件。