1) low water cement ratio
低水灰比
1.
Hydrated performance and microstructure of portland cement with low water cement ratio;
低水灰比下硅酸盐水泥的水化性能和微观结构
2.
The hydration degree of Portland cement under the condition of low water cement ratio was tested,and the microstructure of hardened cement paste was studied by means of XRD and SEM.
研究了低水灰比硅酸盐水泥的水化程度,并利用XRD和SEM分析了硬化水泥浆体的微观结构。
2) medium and low water-cement ratio
中低水灰比
3) low water ratio cement
低水灰比水泥浆
5) low polymer cement ratio
低聚灰比
1.
The study on compound modified method with ground fine mineral powder and emulsion powder to the performance of polymer cement mortar with low polymer cement ratio is carried out.
：采用磨细矿粉与乳胶粉复合改性的方法对低聚灰比聚合物水泥砂浆的性能进行了研究。
6) W/C
水灰比
1.
Influence of W/C for volume method in the design of mixture proportion;
水灰比在采用体积法进行透水混凝土配合比设计中的作用
2.
By mixing the self-matching air-entrancing agent and admixture technique,it researched on the effects of air entrancing quanlity,fly ash quanlity,mortar paste ratio,W/C on the fluidity and strength of EPS light concrete.
采用掺加自配引气剂和掺合料技术,研究引气剂掺量、粉煤灰掺量、胶砂比、水灰比对EPS轻混凝土的流动性以及强度的影响。
3.
This article tries to discuss the effect on concrete setting-time in the aspects of water requirement,W/C,the use of fly ash and admixture.
在预拌混凝土的生产中混凝土的凝结时间是一项重要的技术指标 ,本文试图讨论用水量、水灰比、粉煤灰和外加剂等因素对混凝土凝结时间的影响。
补充资料：水灰比
分子式：
分子量：
CAS号：
性质：拌制水泥浆、砂浆、混凝土时所用的水和水泥的重量之比。水灰比影响混凝土的流变性能、水泥浆凝聚结构以及其硬化后的密实度，因而在组成材料给定的情况下，水灰比是决定混凝土强度、耐久性和其他一系列物理力学性能的主要参数。对某种水泥就有一个最适宜的比值，过大或过小都会使强度等性能受到影响。
分子量：
CAS号：
性质：拌制水泥浆、砂浆、混凝土时所用的水和水泥的重量之比。水灰比影响混凝土的流变性能、水泥浆凝聚结构以及其硬化后的密实度，因而在组成材料给定的情况下，水灰比是决定混凝土强度、耐久性和其他一系列物理力学性能的主要参数。对某种水泥就有一个最适宜的比值，过大或过小都会使强度等性能受到影响。