1) o-cresol formaldehyde epoxy acrylate
邻甲酚醛环氧丙烯酸酯
1.
For raising heat resistance of the anaerobic adhesives,o-cresol formaldehyde epoxy acrylate(o-CFEAR)have been prepared through a two step method.
为提高厌氧胶的热性能,用二步法合成了邻甲酚醛环氧丙烯酸酯(o-CFEAR),并以该树脂为单体,不饱和笼型倍半硅氧烷(POSS)为耐高温改性剂,选择合适的氧化还原体系及其它助剂,制成耐高温厌氧胶,测定了相关性能,研究了该胶的固化动力学。
2.
The effects of three catalysts and their contents on the modification reaction of o-cresol formaldehyde epoxy acrylate with maleic anhydride were investigated.
用马来酸酐对邻甲酚醛环氧丙烯酸酯进行酸改性,考察了3种催化剂及其用量对反应的影响。
2) novolac epoxy acrylate
酚醛环氧丙烯酸酯
1.
By using acrylic acid to modify the F-51 novolac epoxy resin, novolac epoxy acrylate with photosensitive character can be synthesized, which is then induct the carboxyl groups in its molecular chain for good ability of alkali developable by using maleic anhydride.
采用丙烯酸类单体改性F 5 1型酚醛环氧树脂的方法 ,合成具有光固化特性的酚醛环氧丙烯酸酯树脂 ,再用马来酸酐进行改性 ,在分子链上引入羧基 ,使树脂具有良好的碱溶性。
3) o-cresol (2-methylphenol) novolac epoxy acrylate resin
邻甲酚环氧丙烯酸树脂
4) Formaldehyde, polymer with (chloromethyl)oxirane, 4,4'-(1-methylethylidene)bis[phenol] and 2-methylphenol, 2-methyl-2-propenoate
甲醛与(氯甲基)环氧乙烷、4,4'-(1-甲基亚乙基)双酚和2-甲基-2-丙烯酸-2-甲酚酯的聚合物
5) bisphenol A epoxy acrylate resin
双酚A环氧丙烯酸酯树脂
6) m-phendiol epoxy acrylate
丙烯酸间苯二酚环氧酯
1.
he reaction mechanism and kinetics of m-phendiol epoxy acrylatesynthesis catalyzed by dimethylbenzylamine (DMBA) have been studied.
Ｎ，Ｎ－二甲基苄胺催化合成丙烯酸间苯二酚环氧酯的机理高俊刚，王洪芳，袁翠红（河北大学化学系，保定０７１００２）关键词丙烯酸间苯二酚环氧酯，Ｎ，Ｎ－二甲基苄胺，催化反应机理不饱和酸环氧酯是由不饱和核酸与环氧化合物进行环氧化反应形成的一种。
补充资料：环氧乙酰蓖麻油酸甲酯
分子式：C21H38O5
分子量：370.54
CAS号：暂无
性质：淡黄色油状液体。相对密度0.950-0.970，折光率1.458。
制备方法：以蓖麻油和甲醇为原料、先以苛性钠为催化剂醇解，得蓖麻油酸甲酯，再经乙酰化和环氧化，即得产品。原料消耗（kg/t）蓖麻油（工业品） 1170甲醇（工业品） 135乙酐（工业品） 330双氧水（工业品） 390
用途：该品为聚氯乙烯增塑剂。热、光稳定性好，耐寒性优良，透明度高，毒性小。
分子量：370.54
CAS号：暂无
性质：淡黄色油状液体。相对密度0.950-0.970，折光率1.458。
制备方法：以蓖麻油和甲醇为原料、先以苛性钠为催化剂醇解，得蓖麻油酸甲酯，再经乙酰化和环氧化，即得产品。原料消耗（kg/t）蓖麻油（工业品） 1170甲醇（工业品） 135乙酐（工业品） 330双氧水（工业品） 390
用途：该品为聚氯乙烯增塑剂。热、光稳定性好，耐寒性优良，透明度高，毒性小。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。