1) impregnating drug loading
浸渍包埋法
2) vacuum paraffin embedding method
真空浸蜡包埋法
3) dip film-coating
浸渍包膜
4) impregnation method
浸渍法
1.
The mesoporous silicas were impregnated by vion solution and calcined in air at 400 °C,the investigation indicated not only vanadium in samples prepared by impregnation method was incorporated into the famework of mesoporous silicas,but also some dispersed spontaneously onto the surface of mesoporous silicas,and formed a monolayer if total amount of V2O5 increased.
采用X射线衍射技术(XRD)考察了金属氧化物V2O5在介孔二氧化硅分子筛上的分散,研究结果表明应用浸渍法将V2O5浸渍于介孔二氧化硅分子筛中,在低于V2O5熔点的适当温度下焙烧后,与未浸渍V2O5样品相比,晶胞参数a值明显增大,说明钒离子掺入了介孔二氧化硅分子筛的骨架中;在一定范围内随着V2O5加入量的增加其在介孔二氧化硅的表面的分散量也在增加,而V2O5残余晶相量远远低于加入的量,说明V2O5掺入介孔二氧化硅分子筛骨架的同时可在介孔二氧化硅的表面成单层分散。
2.
Silica-supported H_3PW_ 12 O_ 40 catalysts were prepared by the impregnation method, sol-gel technique, and sol-gel technique using ionic liquids as the template, respectively, to solve the problems of H_3PW_ 12 O_ 40 such as low surface area, difficult separation, and reuse.
针对H3PW12O40(HPW)的比表面积小和不易回收利用等缺点,分别采用浸渍法、溶胶-凝胶法和以离子液体为模板剂的溶胶-凝胶法制备了HPW/SiO2催化剂,采用傅里叶变换红外光谱、X射线衍射、N2物理吸附和吸附氨的程序升温脱附等技术对催化剂样品进行了表征,并考察了其对苯硝化反应的催化性能。
3.
Eu-doped TiO2 samples were prepared by the sol-gel method,and further doping which uses ammonia as nitrogen source were carried out by the impregnation method.
本文采用溶胶-凝胶法制备了Eu的TiO2粉体,然后以NH3为N源,采用浸渍法进一步对其处理,获得了同时掺杂Eu、N的纳米TiO2。
5) dipping
[英][dip] [美][dɪp]
浸渍法
1.
This experiment studied the influence of sorption by the concentration, the time of dipping and the time of adsorption.
用浸渍法将活性Al2O3、13A分子筛及活性炭制成负载铜离子的负载型吸附剂来吸附煤油中的硫醇类硫。
2.
The sol-gel dipping method has been used to manufacture TiO2-SiO2 multilayer.
报道了用浸渍法制备的ＴｉＯ２－ＳｉＯ２选择透过膜和这种薄膜与Ｆｅ２Ｏ３－Ｃｒ２Ｏ３－ＭｎＯ２选择吸收涂层的复合徐层。
6) Dipping method
浸渍法
1.
Silver and praseodymium co-doped titanium oxide[(Ag,Pr)/TiO2]nanometer materials were prepared by the dipping method using Pr(NO3)3.
5H2O]、硝酸银(AgNO3)为掺杂的前驱物,纳米二氧化钛(TiO2)为载体,用表面浸渍法制备了(银,镨)/氧化钛[(Ag,Pr)/TiO2]纳米材料。
2.
Using fiber glass cloth as the carrier,the titania photo-catalyst coated on fiber glass cloth was prepared by the dipping method and the adhesive method.
以玻璃纤维布为载体,分别用浸渍法和黏结剂法制备了负载型TiO2光催化剂,用SEM观察了2种方法中TiO2在玻璃纤维表面的负载情况。
补充资料：包埋培养
分子式：
CAS号：
性质：细胞固定化培养的一种。首先用于微生物发酵，具有保护性强、可重复使用、易于连续操作、生长速度快、产品较纯等优点。对于动物细胞，无论是悬浮和贴壁生长的细胞都适用。细胞生长密度高，抗剪切力和抗污染能力强。对悬浮培养的细胞常用海藻酸钙包埋，对贴壁生长的细胞常用胶原包埋。包埋培养的操作步骤简单，条件温和，细胞和多聚物或单体混合，随着凝胶的形成，细胞嵌入多聚物的网格中。有许多多聚物可采用，如聚丙烯酰胺、聚氨酯、海藻酸盐、卡拉胶、琼脂糖等，故通常可选择合适的系统，使细胞处于活性状态。它也存在一些缺点，如扩散限制，并非所有细胞都能接触最佳基质浓度。由于大分子基质不能渗透通过多聚物网格，因而有一些物质被排斥在外。
CAS号：
性质：细胞固定化培养的一种。首先用于微生物发酵，具有保护性强、可重复使用、易于连续操作、生长速度快、产品较纯等优点。对于动物细胞，无论是悬浮和贴壁生长的细胞都适用。细胞生长密度高，抗剪切力和抗污染能力强。对悬浮培养的细胞常用海藻酸钙包埋，对贴壁生长的细胞常用胶原包埋。包埋培养的操作步骤简单，条件温和，细胞和多聚物或单体混合，随着凝胶的形成，细胞嵌入多聚物的网格中。有许多多聚物可采用，如聚丙烯酰胺、聚氨酯、海藻酸盐、卡拉胶、琼脂糖等，故通常可选择合适的系统，使细胞处于活性状态。它也存在一些缺点，如扩散限制，并非所有细胞都能接触最佳基质浓度。由于大分子基质不能渗透通过多聚物网格，因而有一些物质被排斥在外。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条