1) Al_2O_3-TiC-Co
Al2O3-TiC-Co
1.
Al_2O_3-Co+TiC-Co composite powder prepared by electroless plating method was sintered into the ultra-toughen Al_2O_3-TiC-Co cermet by hot pressing technique.
热压烧结化学镀法获得的Al2O3-Co+TiC-Co复合粉体制备超韧Al2O3-TiC-Co复合陶瓷。
2) cobalt-coated Al2O3/TiC composites
Co包覆Al2O3/TiC复合材料
3) TiC-Al_2O_3
TiC-Al2O3
1.
Diffusion bonding of ceramic matrix composite TiC-Al_2O_3 and tool steel W18Cr4V was successfully carried out by addition of composite interlayer Ti/Cu/Ti at 1 130 ℃ for 1 h with a pressure of 15 MPa.
通过添加Ti/Cu/Ti复合中间层,控制加热温度1 130℃,保温1 h,连接压力15 MPa,实现陶瓷基复合材料TiC-Al2O3与高速钢W18Cr4V的真空扩散连接,TiC-Al2O3/W18Cr4V接头抗剪强度达103 MPa。
4) TiC-Al_2O_3 ceramic
TiC-Al2O3陶瓷
1.
Study on crack-healing and its effect on strength of TiC-Al_2O_3 ceramics
XRD衍射分析表明,热处理使TiC-Al2O3陶瓷中的TiC发生氧化反应,生成TiO2填充裂纹是材料愈合和抗弯强度提高的主要原因;治愈温度超过800℃后,锐钛矿TiO2转变为金红石TiO2时产生裂纹,降低了材料的强度。
5) TiCAl_2O_3/W18Cr4V joint
TiC-Al2O3/W18Cr4V接头
6) Co-Cr/Al_(2)O_(3)
Co-Cr/Al2O3
补充资料：WC-TiC-Co hard alloy
分子式：
CAS号：
性质：又称钨钛钴合金或YT合金。碳化钨、碳化钛和金属钴组成的合金。按碳化钛含量，可分为高钛(25％～40％)、中钛(10％～20％)和低钛(4％～6％)三类合金。它比碳化钨钴合金具有较高的抗氧化性，硬度和耐磨性，而抗弯强度、冲击韧性等则有所降低。主要用作切削加工钢材的工具。