1) bainitic lath
贝氏体板条
2) bainite ferrite
板条贝氏体
1.
It is shown that there are different microstructures under two kinds of cooling rate of as rolled steel,and bainite ferrite microstructure obtained by accelerated cooling has higher strength than granular bainite microstructure after.
结果显示,钢轧后,在两种冷速下得到的组织形貌差别较大,快速水冷得到强度较高的板条贝氏体组织,缓冷得到强度较低的粒状贝氏体组织,粒状贝氏体的形成温度较高,没有明显板条特征;板条贝氏体屈服强度比粒状贝氏体高出278MPa,抗拉强度高出307MPa;而粒状贝氏体的塑性和韧性指标明显优于板条贝氏体,延伸率和-20℃低温冲击功指标是板条贝氏体的近3倍。
2.
Mechanical properties of phase transformation microstructure of ULCB steel,including granular bainite and bainite ferrite have been contrasted.
对ULCB钢的主要相变组织粒状贝氏体与板条贝氏体进行了力学性能比较,结果显示粒状贝氏体与板条贝氏体是完全不同的两种组织,较高温度相变产物粒状贝氏体组织较为粗大,对强度和韧性有不利影响,而较低温度相变产物板条贝氏体组织对强度和韧性是有益的。
3) sheaf of bainitic lath
贝氏体板条束
4) lath bainitic ferrite
板条贝氏体铁素体
1.
The experimental results showed that the microstructure of low Nb content steel is composed of polygon ferrite and some amount of lath bainitic ferrite and few amount of pearlite.
结果表明,低铌钢热处理后组织为多边形铁素体加少量板条贝氏体铁素体加极少量珠光体,随着铌含量增加,试验钢组织中板条贝氏体铁素体含量明显增加,且组织细化;同时随着铌含量的增加强度提高,中高铌试验钢的屈服强度可达400 MPa,且屈强比较小(<0。
5) bainite-ferrite strip
贝氏体铁素体板条
6) bainitic welding rod
贝氏体焊条
1.
In order to solve the traditional bainitic welding rod build-up welding rail when preheating before welding and heat treatment after welding, U71Mn rail was directly welding repaired using bainitic welding rod.
为了解决传统焊条在堆焊铁路钢轨时焊前必须预热、焊后进行热处理等不足,本文采用自制的贝氏体焊条对U71Mn钢轨进行直接堆焊修复,分析研究了在不同的电流下直接堆焊钢轨其组织、性能的变化。
补充资料：奥氏体-贝氏体球铁
分子式：
CAS号：
性质：又叫奥-贝球铁。基体组织为奥氏体加贝氏体组织的球墨铸铁。这类球铁硅含量一般在1.4%～3.8%。含锰量小于0.5%，与普通球铁比较硅偏高、锰偏低。通过调节化学成分与热处理获得理想的奥-贝球铁的基体组织为针状贝氏体或无碳贝氏体一富碳奥氏体。这类球铁具有优良的综合机械性能、强度高、耐磨性好、韧性好、特别是有高的缺口韧性，可代替钢，用于制作重要受力结构件，如曲轴、齿轮、凸轮轴等。
CAS号：
性质：又叫奥-贝球铁。基体组织为奥氏体加贝氏体组织的球墨铸铁。这类球铁硅含量一般在1.4%～3.8%。含锰量小于0.5%，与普通球铁比较硅偏高、锰偏低。通过调节化学成分与热处理获得理想的奥-贝球铁的基体组织为针状贝氏体或无碳贝氏体一富碳奥氏体。这类球铁具有优良的综合机械性能、强度高、耐磨性好、韧性好、特别是有高的缺口韧性，可代替钢，用于制作重要受力结构件，如曲轴、齿轮、凸轮轴等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条