1) copolymer emulsion
共聚物乳液
1.
The title core-shell structure of acrylate copolymer emulsion with rich fluorine in shell was prepared using SDS and OP-10 as emulsifier,methyl methylacrylate(MMA),fluoromonomer(Actyflon-Go4)and butyl acrylate(BA) as monomers.
以十二烷基硫酸钠(SDS)和壬基酚聚氧乙烯基醚(OP-10)为复合乳化剂,甲基丙烯酸十二氟庚酯(Actyflon-Go4)、甲基丙烯酸甲酯(MMA)、丙烯酸丁酯(BA)为原料制备了壳层含氟的核壳型丙烯酸酯共聚物乳液。
2.
BA/MMA/MAA copolymer emulsion was carried out with composite emulsifier which consisted of lauryl sodium sulfate(SDS) and octyl polyethoxy(OS 15).
分别合成了固含量 70 %、67%左右的 BA/ MMA/ HAM、BA/ MMA/ MAA共聚物乳液。
3.
A new kind of ferrocene structural unit contained copolymer emulsion with good thermostability is formulated with butyl acrylate,ferrocene allyl formate,methyl acrylic acid and methyl methacrylate.
以丙烯酸丁酯、二茂铁单甲酸烯丙酯、甲基丙烯酸及甲基丙烯酸甲酯为原料制备了新型、对热稳定的含二茂铁单元的共聚物乳液,研究了共聚工艺,并对所制备的乳液进行了表征。
3) quadripolymer latex
四元共聚物乳液
4) copolymer emulsion
三元共聚物乳液
1.
Study on synthesis and properties of perfluoroacrylates copolymer emulsion;
全氟丙烯酸酯三元共聚物乳液的合成及性能研究
6) emulsion copolymerization
乳液共聚
1.
Study on emulsion copolymerization of methyl methacrylate and N-p-tolylmaleimide;
MMA/N-对甲苯基马来酰亚胺乳液共聚的研究
2.
In order to prepare the crosslinking polymer microbeads, the free radical emulsion copolymerization of methylmethacrylate (MMA), acrylonitrile (AN) and divinylbenzene (DVB) with the initiator potassium persulphate (KPS) at 75℃ under constant stirring speed was investigated.
为制备甲基丙烯酸甲酯(MMA)-丙烯腈(AN)-二乙烯基苯(DVB)刚性微粒,在75℃、过硫酸钾(KPS)作引发剂、恒搅拌速率下研究了MMA/AN/DVB乳液共聚动力学,考察了KPS用量、单体配比、交联剂DVB对共聚速率的影响。
3.
VAc/VeoVa10 emulsion copolymerization was studied using sodium dodecyl sulfonate (SDS) as an emulsifier, potassium persulfate (KPS) as an initiator and PVA as a protective colloid.
以十二烷基硫酸钠为乳化剂,聚乙烯醇为保护胶体,过硫酸钾为引发剂,进行醋酸乙烯酯-叔碳酸乙烯酯(VAc-VeoVa10)乳液共聚。