1) fretting wear behavior
微动磨损性能
1.
Surface morphologies and microstructures were observed by scanning electron microscope and transmission electron microscope, their micro mechanical properties were examined by nano indentation, and fretting wear behavior from room temperature to 500 was investigated on a PLINT fretting wear test rig.
01GPa和5GPa,从而改善了镀层的微动磨损性能;复合镀层的耐磨性能约为镍镀层的2倍,这是由于纳米SiO2颗粒对复合镀层具有超细晶强化、硬质点弥散强化以及高密度位错强化机制所致。
2) fretting friction and wear behavior
微动摩擦磨损性能
3) electrical sliding wear resistance
电滑动磨损性能
1.
The trace RE addition improves the electrical sliding wear resistance of the alloys and the highest drop value of the wear rate is 9.
添加微量稀土元素对合金的电滑动磨损性能有改善作用,最高可使磨损率下降9。
4) rolling wear properties
滚动磨损性能
1.
By WM-1 rolling wear machine, which can simulate work condition of the cold roll, the rolling wear properties were measured after different heat treatment.
本文以河南省耐磨材料工程技术研究中心开发的一种成分的高钒高速钢为基础，在淬火温度为900～1100℃，回火温度为250～600℃的条件下进行热处理，测定热处理后试样的机械性能；利用自制的模拟冷轧辊实际工况的WM-1型滚动磨损试验机，测定经不同热处理工艺处理后试样的滚动磨损性能；应用SEM，分析了热处理工艺对其显微组织的影响；应用X射线衍射仪测量了高钒高速钢的残余奥氏体含量；并采用SEM和TEM，探讨了高钒高速钢滚动磨损机制。
6) sliding wear behavior
滑动磨损性能
1.
The influence of heat treatment on phase structure and sliding wear behavior was investigated.
采用粉芯丝材和高速电弧喷涂技术得到的铁铝金属间化合物涂层 ,研究了 5 5 0℃和 80 0℃热处理对涂层相组成及滑动磨损性能的影响。
补充资料：微动磨损
在相互压紧的金属表面间由于小振幅振动而产生的一种复合型式的磨损。在有振动的机械中，螺纹联接、花键联接和过盈配合联接等都容易发生微动磨损。一般认为，微动磨损的机理是：摩擦表面间的法向压力使表面上的微凸体粘着。粘合点被小振幅振动剪断成为磨屑，磨屑接着被氧化。被氧化的磨屑在磨损过程中起着磨粒的作用，使摩擦表面形成麻点或虫纹形伤疤。这些麻点或伤疤是应力集中的根源，因而也是零件受动载失效的根源。根据被氧化磨屑的颜色，往往可以断定是否发生微动磨损。如被氧化的铁屑呈红色，被氧化的铝屑呈黑色，则振动时就会引起磨损。有氧化腐蚀现象的微动磨损也称微动磨蚀。在交变应力下的微动磨损称为微动疲劳磨损。微动磨损的特点是：在一定范围内磨损率随载荷增加而增加，超过某极大值后又逐渐下降；温度升高则磨损加速；抗粘着磨损好的材料抗微动磨损也好；零件金属氧化物的硬度与金属硬度之比较大时，容易剥落成为磨粒，增加磨损；若氧化物能牢固地粘附在金属表面，则可减轻磨损；一般湿度增大则磨损下降。在界面间加入非腐蚀性润滑剂或对钢进行表面处理，可减小微动磨损。螺纹联接加装聚四氟乙烯垫圈也可减小微动磨损。