1) nylon1010/66 copolymer
PA1010/66共聚物
1.
Two kinds of plasticizers DIDP,BSBA and toughness agent SEBS-g-MAH were used in the preparation of nylon1010/66 copolymer/SEBS-g-MAH/DIDP/BSBA blends by means of blending extrusion.
将尼龙(PA)1010盐和PA66盐按照质量比为9∶1的比例制备了PA1010/66共聚物。
2) thermal gravimetric analysis (TG)
PA1010/6共聚物
3) Nylon 1212/66 Copolymer
尼龙1212/66共聚物
4) nylon 1010/66 copolymer
尼龙1010/66共聚物
1.
It has been studied by PLM and DSC that the thermodynamic parameters such as melting point, melting temperature range, melting heat and entropy fo nylon 1010/66 copolymers are related to their compositioms.
本文研究了尼龙1010/66共聚物的熔点、熔程、熔融热和熔融熵等热力学参数与其组成的关系,其相图中最低共熔点时尼龙1010重量比为60～70％,与理论值相近,此时熔点、熔融热和熔融熵最低,熔程最大。
5) nylon6/66 copolymer
尼龙6/66共聚物
1.
The applications of electrospun nylon6/66 copolymer nonwovens fabrics are limited because of contraction in water.
通过静电纺丝制备的尼龙6/66共聚物纳米纤维毡在水中的结构和尺寸稳定性差,这阻碍了产品的实际应用。
6) PA1010/PS blend
PA1010/PS共混物
补充资料：PA/PSU blend
分子式：
CAS号：
性质：聚砜(PSU)和PA66或PA6经适当共混得到的新型高分子材料。这种材料中尼龙为基体，PSU分散于其中，加入PSU改进了PA的耐热性，降低其吸水性，而保留了尼龙的易加工和耐化学品特性。以Amoco产品为例，共混物含50％的尼龙6，40％的PSU，10％特种增容剂，其拉伸强度67MPa，断裂伸长率124％，热变形温度(1.82MPa负荷)112℃。采用机械共混法制备共混时需要加入特种增容剂如端基含酸酐基的聚砜，其酸酐基在熔融机械共混时能和尼龙反应。可以注射、挤出成型及纺丝，用于电子工业、汽车工业各种零件。
CAS号：
性质：聚砜(PSU)和PA66或PA6经适当共混得到的新型高分子材料。这种材料中尼龙为基体，PSU分散于其中，加入PSU改进了PA的耐热性，降低其吸水性，而保留了尼龙的易加工和耐化学品特性。以Amoco产品为例，共混物含50％的尼龙6，40％的PSU，10％特种增容剂，其拉伸强度67MPa，断裂伸长率124％，热变形温度(1.82MPa负荷)112℃。采用机械共混法制备共混时需要加入特种增容剂如端基含酸酐基的聚砜，其酸酐基在熔融机械共混时能和尼龙反应。可以注射、挤出成型及纺丝，用于电子工业、汽车工业各种零件。