1) anti-reversion
抗硫化返原性能
1.
The results showed that the sulfur/LaDiPDP curing stytem obviously improved the vulcanization rate and anti-reversion property of NR compound;the curing rate and curing state were increased as the addition level of LaDiPDP increased;the curing temperature could be enhanced up to 160 ℃.
与常用促进剂BZ,TMTD,DM和NOBS相比,促进剂LaDiPDP具有适中的硫化速度和较好的抗硫化返原性能。
2.
The results showed that the dynamic properties,especially the anti-reversion of vulcanizate improved by adding anti-recovery agent PK900 in shoulder pad without any adverse effect on curing behaviour of rubber compound and physical properties of vulcanizate.
结果表明,在胎肩垫胶中加入抗硫化返原剂PK900,可以明显提高胶料的抗硫化返原性能,改善硫化胶的动态性能,对胶料的硫化特性和硫化胶的物理性能无明显影响。
3.
)The results showed that M_H of rubber compound increased and the heat build-up decreased by adding anti-recovery agent Z500;at the same time the anti-reversion and the main physical properties of vulcanizate,especially the heat aging property and compression fatigue property of overcured vulcanizate improved.
结果表明,加入抗硫化返原剂Z500,可以增大胶料的MH,降低胶料生热,改善胶料的抗硫化返原性能,提高硫化胶的主要物理性能、过硫化胶的耐热老化性能及压缩疲劳性能。
2) anti-reversion
抗硫化返原性
1.
The results showed that the processibility of rubber compound was significantly improved,at the same time the anti-reversion was increased,the energy consumption was decreased without affecting the physical properties of vulcanizate by adding anyone of the said processing aids.
该类加工助剂对改善橡胶的加工特性有显著的效果 ,同时可提高抗硫化返原性 ,降低能耗 ,对硫化胶物理性能影响不大 ,是一种综合效果较好的加工助
3) overcure-reversion
硫化返原性
1.
The results show that the addition of struktol A-73 to the compound has the following advantages: improved overcure-reversion resistance and thermal stability, Increasead efficiency of vulcanizaimproved dynamic performance, lower heat build-up and compression set, freefrom thepotential pollution of nitrosamine, minimal adverse effect on the adhesion with steel cord after aging.
研究了活化剂ＳｔｒｕｋｔｏｌＡ－７３在天然橡胶及天然橡胶与丁苯橡胶并用胶中的应用特性，结果表明：胶料中加入ＳｔｒｕｋｔｏｌＡ－７３可改善胶料的抗硫化返原性和热稳定性；提高胶料的硫化效率；改进胶料的动态性能；降低胶料的生热和压缩永久变形；与噻唑类硫化促进体系并用，无亚硝胺污染环境的危险；对钢丝粘合性能造成的影响，在胶料老化之后即可降至最小；混炼工艺性能良好。
4) anti-reversion agent
抗硫化返原剂
1.
Effect of anti-reversion agent on properties of steel cord bonding compound;
抗硫化返原剂对钢丝粘合胶性能的影响
2.
Study on application of anti-reversion agent in TBR tire;
抗硫化返原剂在载重子午线轮胎中的应用研究
3.
Study on reversion course of NR and mechanism of new anti-reversion agent Z-500 by FTIR;
用FTIR研究NR硫化返原过程和新型抗硫化返原剂Z-500作用机理
5) anti recovery agent
抗硫化返原助剂
1.
The reversion kinetics of NR,the mechanism of anti recovery agent,the optimum levels of different anti recovery agents in different compounding formulas and their effects on the physical properties of vulcanizates are reviewed.
对硫化返原的动力学、抗硫化返原助剂的作用机理、不同抗硫化返原助剂在不同的配合体系中的用量及对硫化胶性能的影响进行评述。
6) anti-recovery agent
抗硫化返原剂
1.
Application of anti-recovery agent PK900 in shoulder pad of BTR tire;
抗硫化返原剂PK900在全钢载重子午线轮胎胎肩垫胶中的应用
2.
Application of anti-recovery agent DL-268 in shoulder pad of 11.00-20 18PR tire;
抗硫化返原剂DL-268在11.00-20 18PR轮胎胎肩垫胶中的应用
3.
Study on application of anti-recovery agents in pure natural rubber compounds;
抗硫化返原剂在纯天然橡胶复合体系中的应用研究
补充资料：返原
分子式：
CAS号：
性质：长时间热老化所引起的硫化橡胶模量和拉伸强度的下降。发生返原的原因可能是网状结构被破坏而形成一些环状结构。天然橡胶或合成聚异戊二烯当硫化时间过长或温度超过150℃时，时常会发生返原现象。
CAS号：
性质：长时间热老化所引起的硫化橡胶模量和拉伸强度的下降。发生返原的原因可能是网状结构被破坏而形成一些环状结构。天然橡胶或合成聚异戊二烯当硫化时间过长或温度超过150℃时，时常会发生返原现象。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。