1) stainless steel clad plate
不锈钢复合板
1.
According to clad metal characteristics,the welding experiment of stainless steel clad plate 16MnR+316L are conducted,from what has been done above,the welding practice is made up,the welding quality is guaranteed and the welding efficiency is increased.
根据不锈钢复合板的特性,分析了16MnR+316L不锈钢复合板的焊接性,对焊接工艺进行了评定试验,确定了焊接工艺,保证了设备的焊接质量,提高了焊接效率。
2.
The stainless steel clad plate,whose base is 20MnMoNb and cladding is import 304 steel plate,appears serious crack after a large explosion,but its cladding doesn't crack.
基层为20MnMoNb、复层为进口304钢板的不锈钢复合板,其爆炸后基层出现了严重开裂,但复层未裂的问题。
2) stainless clad strip
不锈钢复合板
1.
We study the cool rolling of stainless clad strips in bimetal composite plates.
研究了双金属复合板中不锈钢复合板的冷轧生产工艺,并用大型有限元软件ANSYS模拟了不锈钢复合板的冷轧过程。
3) stainless clad plate
不锈钢复合板
1.
A research on the interfacial structure and performance of stainless clad plate 0Cr18Ni9-08Al-0Cr18Ni9 has been made in different states by using optical microscope and SEM,to offer a theoretical and experimental base for improving and selecting a reasonable technology for producing stainless clad plate.
采用光学显微镜、扫描电镜等手段,对0C r18N i9-08A l-0C r18N i9不锈钢复合板在不同状态下的界面组织结构及其性能进行了研究,以期为改进和选择合理的生产工艺提供可靠的理论和实验依据。
2.
The prospect of stainless clad plate is promising.
不锈钢复合板具有广阔的发展前景,焊接技术是其推广应用的关键技术。
4) Clad Plate of Stainless Steel
不锈钢复合板
1.
Discussion on manufacturing technology and weldability for clad plate of stainless steel;
不锈钢复合板制备技术及其焊接性探讨
5) stainless clad sheet
不锈钢复合板
1.
The manufacture craft of stainless clad sheet was carried out in this paper and the multi-pass hot-rolling process of stainless clad sheet was simulated using the finite-element software MARC.
本文讨论了Q235/304不锈钢复合板的生产工艺,并用有限元软件Marc模拟了不锈钢复合板的多道次热轧过程。
6) Stainless Steel Compound Plate
不锈钢复合钢板
1.
On Welding of Stainless Steel Compound Plate 16MnR+00Cr19Ni10;
16MnR+00Cr19Ni10不锈钢复合钢板的焊接
补充资料：不锈钢板
分子式：
分子量：
CAS号：
性质：按制法分热轧和冷轧的两种，包括厚度0.5-4毫米的薄板和4.5-35毫米的厚板。按钢种的组织特征分为5类：奥氏体型、奥氏体-铁素体型、铁素体型、马氏体型、沉淀硬化型。要求能承受草酸、硫酸-硫酸铁、硝酸、硝酸-氢氟酸、硫酸-硫酸铜、磷酸、甲酸、乙酸等各种酸的腐蚀，广泛用于化工、食品、医药、造纸、石油、原子能等工业，以及建筑、厨具、餐具 、车辆、家用电器各类零部件。为了保证各类不锈钢板的屈服强度、抗拉强度、伸长率和硬度等力学性能符合要求，钢板交货前必须经过退火、固溶处理、时效处理等热处理。
分子量：
CAS号：
性质：按制法分热轧和冷轧的两种，包括厚度0.5-4毫米的薄板和4.5-35毫米的厚板。按钢种的组织特征分为5类：奥氏体型、奥氏体-铁素体型、铁素体型、马氏体型、沉淀硬化型。要求能承受草酸、硫酸-硫酸铁、硝酸、硝酸-氢氟酸、硫酸-硫酸铜、磷酸、甲酸、乙酸等各种酸的腐蚀，广泛用于化工、食品、医药、造纸、石油、原子能等工业，以及建筑、厨具、餐具 、车辆、家用电器各类零部件。为了保证各类不锈钢板的屈服强度、抗拉强度、伸长率和硬度等力学性能符合要求，钢板交货前必须经过退火、固溶处理、时效处理等热处理。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条