1) martensite isothermal quenching
马氏体等温淬火
2) marquenching
马氏体等温淬火，热浴淬火，间歇淬火，马氏体分级淬火
3) bainite isothermal quenching
贝氏体等温淬火
4) austempering
[,ɔ:s'tempəriŋ]
奥氏体等温淬火
5) Bainite quenching
等温淬火，贝氏体淬火
6) quenched martensite
淬火马氏体
1.
The white layer is practically nanocrystalline quenched martensite with great lattice distortion and internal stress.
白亮层的本质是纳米晶淬火马氏体,晶格畸变大,内应力大;另一方面,模具几何尺寸如尖角效应,也产生局部应力集中。
2.
It has been found that the reasor of early fracture of sheller is that the retained austenite was transformed into the quenched martensite and strain induced martensite during the service.
结果表明,造成退壳器早期断裂失效的原因是,零件在低温(-60℃)和循环载荷作用下,在使用期间部分残余奥氏体转变为淬火马氏体及应变诱发马氏体,从而在构件内部产生大量的应力集中源,疲劳裂纹首先萌发于此处,然后快速扩展直至断裂。
3.
The white layer is practically nanocrystalline quenched martensite with great lattice distortion and internal stress.
白亮层的本质是纳米晶淬火马氏体,晶格畸变大,内应力大；另一方面,模具几何尺寸如尖角效应,也产生局部应力集中。
补充资料：35CrNi3MoV钢等温淬火组织
35CrNi3MoV钢等温淬火组织
35CrNi3MoV钢等温淬火组织马氏体(绿)+见氏体(棕)残余奥氏体(浅黄)