1) carburizing steel
渗碳钢
1.
Discussion on grinding method of carburizing steel bearing;
渗碳钢轴承的磨加工方法
2.
The different heat treatment results of several process alloy carburizing steel 18Cr2Ni4W are introduced in the artical,and the reasons of these processes are analyses at the angle of region heat treatment theory.
介绍了合金渗碳钢18Cr2Ni4W几种工艺的热处理效果,并据热处理原理分析了其中的原因,得出淬火后进行深冷处理是18Cr2Ni4W渗碳钢的最佳工艺方法。
3.
The investigation of rolling strengthening on the surface of carburizing steel 20CrMo has been made.
研究了渗碳钢 2 0CrMo表面滚压强化工艺 ,结果表明 ,钢渗碳、淬火、低温回火后进行滚压 ,具有高的多冲接触疲劳抗力 ,在一定深度范围内 ,多冲接触疲劳抗力随滚压层深的增加而提
2) Carburized Steel
渗碳钢
1.
The case hardenability of carburized steels were experimentally investigated and someapplications of isoharness curve are discussed.
本文对渗碳钢的渗层淬透性进行试验研究,并论述了等硬度曲线的某些应用。
3) carbonizing steel
渗碳钢
1.
According to the microalloying and strengthening and toughening principles of steel,a theoretical calculation method and optimum alloying design to determine titanium content in carbonizing steel were proposed.
根据钢铁材料的微合金化原理和强韧化原理,对广泛使用的含钛渗碳钢的钛含量进行了理论计算分析和优化设计,结果表明,适当降低钛含量,不影响其在渗碳过程中阻止奥氏体晶粒长大的作用,但可有效地减少或消除含钛渗碳钢中的液析氮化钛,从而提高钢材的力学性能。
4) aluminizing carbon steel
渗铝碳钢
1.
The influence on aluminizing carbon steel of temperature,partial pressure of CO2,mineralization and pH value was studied through zero-G test.
在高压釜中对N80钢和渗铝碳钢材料进行了CO2腐蚀试验。
5) 18CrMn2SiMo carburizing steel
18CrMn2SiMo渗碳钢
6) aluminized mild steel
碳钢渗铝
1.
The results showed that the susceptibility to H2S corrosion cracking of the weld seam is higher than that of the relevant matrix; the SCC susceptibility of Aluminized Mild Steel is lower than that of steels of 20# and 16MnR; The application of aluminized mild steel to heat exchanger was suggested.
用双U形恒应变实验方法,研究了20#碳钢、16MnR、碳钢渗铝基材及焊接材料浸泡在不同硫化物浓度的油品介质中的开裂敏感性。
补充资料:渗碳钢
分子式:
CAS号:
性质:可经受渗碳淬火使表面硬度和耐磨性提高而心部保持适当强度和韧性的钢。其成分特点是低的含碳量,一般为0.1%~0.25%;主要合金元素有Ni、Cr、Mn等,辅助合金元素有W、Mo、V、Ti等。其热处理的特点是,对于低强度的15Cr和20Cr多则,渗碳后应直接淬火或二次淬火;中强度的20CrMnTi钢渗碳后应直接淬火;高强度的18Cr2Ni4W4钢渗碳后应采取空冷、高温回火,这样能使零件满足其在机械性能上的要求。渗碳钢主要用于制造齿轮、凸轮、活塞销等零件。
CAS号:
性质:可经受渗碳淬火使表面硬度和耐磨性提高而心部保持适当强度和韧性的钢。其成分特点是低的含碳量,一般为0.1%~0.25%;主要合金元素有Ni、Cr、Mn等,辅助合金元素有W、Mo、V、Ti等。其热处理的特点是,对于低强度的15Cr和20Cr多则,渗碳后应直接淬火或二次淬火;中强度的20CrMnTi钢渗碳后应直接淬火;高强度的18Cr2Ni4W4钢渗碳后应采取空冷、高温回火,这样能使零件满足其在机械性能上的要求。渗碳钢主要用于制造齿轮、凸轮、活塞销等零件。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。