1) high temperature aging
高温时效
1.
The evolution of microstructure especially the IMC at high temperature aging process had been systematically investigated and the effect of trace amount rare earth Y also had been studied.
7Cu高温时效过程中显微组织,特别是金属间化合物(IMC)的演化规律,以及稀土Y的添加对其产生的影响。
2.
The results show that the aging response of the experimental alloy is greatly accelerated by high temperature aging,but this treatment decreases the peak aging strength of the alloy.
研究结果表明:合金在250℃时效有很高的时效响应速度,但是,在250℃时效后的峰值强度要明显低于165℃时效的峰值强度;在相同条件下高温时效后的合金在峰值状态的持久寿命最长,并且其持久强度要远远高于低温欠时效态的持久强度;Ω相为合金高温时效后的主要强化相,高温时效抑制了θ′的析出;高温短时间人工时效能够极大地提高合金的高温持久性能。
2) high temperature ageing
高温时效
1.
On the base of producting experiment, this artieal discusses about by the way of high temperature ageing treatment, cancling the miternal stress of optical comp.
本文在总结生产试验的基础上,探讨了利用高温时效精密退火的方法,消除光学零件的内应力,并给出了消除真空镀膜零件内应力的温度时间曲线。
3) high-temperature aging
高温时效
1.
Dissipative structures of heat-resistant steel 12Cr1MoV during high-temperature aging;
耐热钢12Cr1MoV高温时效中的耗散结构
4) aging
[英]['eidʒiŋ] [美]['edʒɪŋ]
高温时效
1.
The sulfidation behavior of 310SS (Stainless Steel) before and affer high-temperature aging treatment has been studied in the gas mixture of 2.
研究了高温时效前后的 31 0不锈钢样品在气氛总压为 1 0 5Pa ,2 。
2.
The results show that Cr and Ni diffuse toward the weld interface while Fe diffuses in the reverse direction; the composition of carbide M23C6 precipitated in carbon-enriched zone is independent of aging time at 5.
利用透射电子显微镜（ＴＥＭ）、能谱仪（ＥＤＸ）和电子探针显微分析仪（ＥＰＭＡ）研究了珠光体钢／奥氏体钢（Ｃｒ５Ｍｏ／Ｃｒ２１Ｎｉ１２）异质焊头在高温时效和长期服役中元素Ｃ，Ｃｒ，Ｎｉ，Ｆｅ的扩散行为结果表明：时效时奥氏体钢中Ｃｒ，Ｎｉ原子向熔合界面方向扩散，Ｆｅ原子向相反的方向扩散；增碳层中析出碳化物Ｍ２３Ｃ６的成分与时效时间无关；增碳层最高含碳量由析出碳化物的类型、成分及紧靠熔合界面奥氏体钢中的Ｃｒ含量决定。
5) elevated temperature aging
高温时效
1.
An Analysis of Atomic Diffusion on Structure Variation of Steel 12Cr1MoV during Elevated Temperature Aging;
12Cr1MoV钢高温时效中组织结构变化的原子扩散分析
6) High-temperature and short-time aging
高温短时时效
1.
The main results were concluded as follows:(1) High-temperature and short-time aging process:①The phases constitutes of K418 alloy have no changes during aging,which are still composed ofγ-austenite,γ′-Ni_3(Al,Ti) and MC-carbide.
本文利用扫描电子显微镜(SEM)、光学显微镜(OPM)和X射线衍射仪(XRD)等实验手段,对涡轮盘材料GH2036和涡轮叶片材料K418高温短时时效模拟处理样品进行了微观组织研究,确定出过热损伤组织形貌特征,并对增压器涡轮盘和涡轮叶片热损伤进行了失效原因分析。
补充资料：高温合金时效强化
高温合金时效强化
age strengthening of super- alloy
g0Owen heJ一n shlxlQO qlanghUQ高温合金时效强化(age Strengthening。fsuperalloy)经过时效热处理，从奥氏体基体中析出一些相使高温合金强化。因为这些相是从基体中析出的，因此有时称为第二相或沉淀相，所以时效强化又称为第二相强化或沉淀强化。用固溶强化手段设置位错运动障碍是不够稳定的，其强化效果也不够强烈。为了更有效地阻碍位错运动，就要利用稳定的障碍物，高温合金通常采用固态析出的时效相，如丫、丫和碳化物(见高温合金材料的间隙相、高温合金材料的金属间化合物相)等作为稳定的障碍物。 从位错理论出发，时效强化效应是和位错与析出相的交互作用密切相关的。运动着的位错与析出相相遇时，其机械障碍作用有4种情况:(l)应力场障碍。时效相析出时会在基体中产生应力场，特别当时效相与基体具有共格关系时，可以产生很高的弹性应力场。(2)位错攀移析出相克服障碍。(3)位错绕过析出相的障碍。位错线在靠近析出相颗粒时受阻变弯，位错线绕过析出相并在其周围留下位错环后才能继续向前运动，这是有名的欧罗万(orowan)机制。(4)位错切割析出相的障碍。位错切割析出相时，增加了它与基体之间的界面而需要做功。如果析出相为有序结构时，当位错切过时会在有序结构中产生反相畴界而需要做功。 丫相是高温合金中最重要的时效强化相。随着丫相数量增加，强化效果增加。在镍基高温合金中，7‘相的数量能达到60纬一65%;而铁基高温合金中只能达到20%左右。铁基高温合金中丫相的合适尺寸是。.01一。，。5卜m，通常呈球形。镍基高温合金中应使丫相的平均间距保持在。.05尸。左右;当丫相含量超过40%时，丫相间距对强化不敏感，此时丫相可以达到很大尺寸(0·却m左右)，形貌为立方体形。 (谢锡善)