1) γ-ray irradiation
γ-射线辐射
1.
The progress in the investigation of controlled/living free radical polymerizations under γ-ray irradiation condition is reviewed.
本文对γ-射线辐射条件下的活性自由基聚合反应进行了综述。
2) gamma rays radiation
γ射线辐射
1.
The novel gamma rays radiation desulfurization method used for petroleum products was investigated.
常规的加氢脱硫方法存在工艺复杂、运行成本高等问题,因而探索了利用γ射线辐射去除油品中硫醚硫的新方法。
2.
A novel desulfurization method for petroleum products by gamma rays radiation is put forward and investigated in this paper.
提出利用γ射线辐射的方法对油品进行脱硫的新技术 ,并以十二硫醇为对象考察了主要工艺条件对脱硫效果的影响 。
3) gamma radiation
γ射线，γ辐射
4) ray line emission
γ射线线辐射
5) γ-ray irradiation
γ-射线辐照
1.
Modification mechanism of PBO fiber surface by γ-ray irradiation;
γ-射线辐照PBO纤维表面改性机理研究
2.
The in situ intercalated polymerization of vinyl acetate (VAc)-montmorillonite (MMT) was initiated via γ-ray irradiation in a 6 kCi ~(60)Co irradiator and got the MMT-PVAc nanocomposites, as well as we got the PVAc.
采用γ-射线辐照法制备了聚醋酸乙烯酯(PVAc)及聚醋酸乙烯酯/蒙脱土(MMT)纳米复合材料。
3.
The effects of γ-ray irradiation on the structure of the solution-grown polyethylene single crystals were studied by means of the infrared spectroscopy , X-ray wide angle diffraction and small angle scattering as well as differential scanning calorimetry on the mixed crystals of polyethylene and deuterated polyethylene.
采用混合晶红外光谱、X-射线衍射及小角散射、差示扫描量热法研究γ-射线辐照对溶液生长聚乙烯单晶的影响,表明γ-射线辐照在单晶的规则折叠区也引起了不可忽视的结构缺陷或畸变。
6) γ-ray Radiation
γ-射线辐照
1.
The γ-ray radiation was used to modify the surface activity of pitch carbon fiber to improve the interfacial adhesion between the fiber and matrix.
为了提高沥青基炭纤维表面活性,采用γ-射线辐照对沥青基炭纤维表面改性。
2.
The γ-ray radiation in A151 was used to modify surface activity of pitch carbon fiber to improve the interfacial adhesion between fibers and matrix in order to decrease porosity and moisture absorption of C/C composites.
为了减少C/C复合材料气孔率、降低C/C复合材料吸湿性,本文采用γ-射线辐照在A151中对沥青基炭纤维表面改性,采用AFM、XPS研究了γ-射线辐照改性后沥青基炭纤维表面结构的变化;用浸润仪测定了改性前后沥青基炭纤维表面能的变化;对γ-射线辐照沥青基炭纤维对C/C复合材料气孔率、吸湿增重的影响进行了研究。
补充资料：抗X射线辐射复合材料
抗X射线辐射复合材料
anti-X-ray composite materials
抗x射线辐射复合材料anti一X一ray compositematerials用于抵抗X射线辐射造成对材料结构的破坏效应的一类复合材料。材料吸收系数是衡量光子和材料作用的能力。它取决于光子能量和材料所含元素的性质。一般讲元素的原子序数越大，吸收系数越大。X射线照射到材料上，则光子与材料的原子发生作用，X射线在物质中迁移时，被物质吸收变成物质的内能，即X射线能量在物质中沉积。同时，X射线能流密度大，释放的时间极短，使材料的比内能急剧增加而升高温度，并且在材料表面处形成很高的压力。结果在材料表面形成一个峰值极高、持续时间极短的压力脉冲一热击波，使材料产生“层裂”效应，同时产生瞬时过载，结构产生变形，乃至破坏。 为了防止X射线的破坏作用，曾提出一种物理模型。它由迎光层、屏蔽层、衰减层和过渡层4层结构组成。衰减层采用泡沫塑料，其他层分别采用碳一酚醛、高硅氧一酚醛等复合材料。利用密度小、质量轻的硅酸盐类多孔复合材料，既可防止大能量的X射线的辐照，同时也是解决能量沉积行为的极好材料。 (于翘)